Influence of Direct Lamellarizing-Tempering Process Parameters on Microstructure and Properties of 9 Ni Steel

XIE Zhang-long,CHEN Jun,LIU Zhen-yu,WANG Guo-dong
DOI: https://doi.org/10.13289/j.issn.1009-6264.2011.05.014
2011-01-01
Abstract:Influence of holding time and tempering time in the direct inter-critical quenching and tempering(DLT) process on microstructure and properties of 9Ni steel was investigated.The results show that under the same tempering conditions,the highest cryogenic toughness is obtained when holding time in inter-critical region is 40 min,which is less than the optimal holding time for QLT process.Higher strength and lower cryogenic toughness are achieved when the holding time is 20 min,and the lowest cryogenic toughness is obtained when holding time is 60 min and remained almost unchange as tempering time increased due to the coarsened microstructure obtained during the long holding time.For the specimens after holding at inter-critical region for 40 min,more reversed austensite is obtained with increasing tempering time,which could hinder the cracking propagation,increase the cryogenic toughness and decrease the strength,which is caused by the precipitation of reversed austensite between martensite blocks to scavenge carbon and other deleterious elements in matrix.
What problem does this paper attempt to address?