Segregation Behavior and Formation Mechanism of 7050 Aluminum Alloy Produced by Semi-Continuous Casting under Ultrasonic Field

LI Zheng-hua,LI Xiao-qian,ZHANG Ming,XU Xian-hua
DOI: https://doi.org/10.19476/j.ysxb.1004.0609.2011.02.011
2011-01-01
The Chinese Journal of Nonferrous Metals
Abstract:The macro-distribution of solute elements Zn and microstructure for 7050 aluminum alloy by semi-continuous casting under the ultrasonic field were investigated by SPECTRO-MAXx and Leica optic microscopy.The results show that the microstructure refines,the duplex structure consisting of coarse-cell and fine-cell dendritic grains decreases,the inverse segregation grade of Zn decreases effectively.With the increase of the ultrasonic power,the microstructure becomes finer and more uniform,the distribution of solute elements is more harmonious,the segregation ratio of Zn through 240 W ultrasonic treatment decreases to 1.086 from 1.190 without ultrasonic.After being treated by ultrasonic field,the nucleation ratio of the Al melt increases,the microstructure refines,the relative velocities of the solid and liquid phases in mushy zone decreases,and the shrinkage-induced flow of the enriched solute decreases due to the sump height decreases,which suppresses macro-segregation in a great degree.The liquid phases flow controlled by ultrasonic field is an effective means to weaken the macro-segregation in semi-continuous casting.
What problem does this paper attempt to address?