Abstract:The 600 °C and 450 °C isothermal sections of the Co-Cu-Zn ternary system have been investigated experimentally by means of scanning electron microscopy coupled with energy dispersive x-ray spectroscopy, and x-ray diffraction. Five three-phase regions were confirmed in the 600 °C isothermal section and six three-phase regions existed in the system at 450 °C. The γ-Co5Zn21 and Γ-Cu5Zn8 phases formed a continuous solid solution, which is designated as the γ/Γ phase. No ternary compound was found in the present work. The solubility of Co in δ and β is up to 1.8 and 8.8 at% respectively, and the maximum solubility of Cu in γ1 and β1 is 14.7 and 7.9 at% respectively at 600 °C. The maximum solubility of Co in ε and β ´ is 8.5 and 6.7 at% respectively, and the solubility of Cu in γ2, γ1 and β1 is up to 12.9, 14.4 and 11.2 at% respectively at 450 °C.

450 °C Isothermal Section of the Zn-Fe-Cu Ternary System

The 620°C and 800°C isothermal sections of the Zn-Fe-Cu ternary system

The Zinc-Rich Corner Of The Fe-Si-Sn-Zn Quaternary System At 450 Degrees C

The Isothermal Section of the Fe-Si-Ti-93 at.% Zn Quaternary System at 450 °C

Experimental Investigation of the 650 °C Isothermal Section of the Cu-Fe-Si Ternary Phase Diagram

The 480°C and 405°C isothermal sections of the phase diagram of Fe–Zn–Si ternary system

Phase equilibria of the Co-Cu-Zn system at 600 °C and 450 °C

The Zn-Rich Corner of the 450 °C Isothermal Section of the Zn-Fe-Ni-Sb Quaternary System

560 °C Isothermal Section of Zn–Fe–Ni System at the Zn-rich Corner

The Zinc-Rich Corner of the Zn-Al-Co-Fe Quaternary System at 450 °C

600°C Isothermal Section of the Zn-Fe-Nb Ternary System at the Zn-Rich Corner

Phase equilibria in the Zn-Fe-S system at 450 °C

The 600 °C and 700 °C Isothermal Sections of the Zn-Fe-Bi Ternary System

Experimental Investigation of the Zn–Fe–V System at 450°C

The Zn-rich Corner of the 450 °C Isothermal Section of the Zn–Bi–Fe–Ni Quaternary System

Ternary Phase Equilibria at 450 °C in the Zn-Fe-P System

The 600 °C and 450 °C Isothermal Sections of the Zn–Fe–B System

Phase Equilibria of the Al–Zn–Fe–V Quaternary System at 620 °C

Phase Equilibria of the Al-Zn-Fe-Ti Quaternary System at 600 °C

450 Degrees C Isothermal Section Of The Zn-Fe-Co-Si Quaternary System At The Zinc-Rich Corner

450°C isothermal section of the Zn-Fe-Co-Si quaternary system at the zinc-rich corner