Abstract:To determine how the performance of concrete changes after initial load damage and salt freezing, concrete samples were first subjected to loading and unloading, and were then put into salt solutions to carry out rapid freeze-thaw cycle (FTC) experiments. Salt solutions were created based on the saline soil of western Jilin, China, for use in salt freeze-thaw testing. This determined the change law of the compressive strength and the dynamic elastic modulus (DEM). Additionally, low-field nuclear magnetic resonance technology and a scanning electron microscope were applied to investigate the pore characteristics and microstructure of concrete samples after FTCs. This study found that when the concrete specimens were subjected to an initial load of 0.3f under 50 FTCs, the loss in the compressive strength increased by 24% when the concrete was subjected to freeze-thaw cycles in freshwater and increased by 24% when concrete was subjected to freeze-thaw cycles in a 6.8% composite salt solution compared with the specimens without the initial load. When the concrete was subjected to FTCs in a 6.8% composite salt solution 50 times, the loss in the compressive strength increased by 110% for concrete without an initial load and increased by 109% when the concrete was subjected to an initial load of 0.3f compared with the specimens under FTCs in freshwater. The persistent effect of the FTCs also aggravated chloride ion erosion in the concrete, which gradually reduced the concrete's permeability resistance. Internal pores in the concrete, especially the proportion of above-medium-sized pores, gradually increased along with the increase in the number of FTCs. There is a good linear correlation between the change rule of compressive mechanical properties and the change rules of mass, DEM, and pore characteristics inside the concrete under rapid FTCs in different salt solutions.

Effect of Saturation Degree on Concrete Deterioration Due to Freeze-Thaw Action

Development of Internal Moisture Transfer and Cumulative Residual Strain in Concrete under Freeze-Thaw Cycles

Deterioration characteristics of the bond between reinforcement and concrete subjected to freezing-thawing cycles and steel corrosion

Environmental Factors Influencing The Durability Of Concrete Structures In Frost Environments

Stress Analysis for Concrete Materials under Multiple Freeze-Thaw Cycles

Experimental Study and Mechanism Analysis on Frost Resistance of Normal Performance Concrete under Different Environments

Experimental Study on Mechanical Properties and Pore Structure Deterioration of Concrete under Freeze–Thaw Cycles

Influence of damage degree on the degradation of concrete under freezing-thawing cycles

Macroscopic and Mesoscopic Deterioration Behaviors of Concrete under the Coupling Effect of Chlorine Salt Erosion and Freezing–Thawing Cycle

Meso-Scale Mechanical Deterioration Of Mortar Subjected To Freeze Thaw Cycles And Sodium Chloride Attack

Investigation of Opening and Closing Water Boundary Conditions on Frost Damage Development in Concrete

An autoregressive modeling approach to analyzing wheelchair propulsion forces.

Deterioration of concrete under the coupling action of freeze–thaw cycles and salt solution erosion

Numerical Simulation of the Effect of Freeze–Thaw Cycles on the Durability of Concrete in a Salt Frost Environment

Experimental Evaluation of the Concrete Damage and Pore Characteristics under Salt-Freezing Cycles

Effect of PVA fiber on the freezing and thawing behavior of concrete

Degradation Mechanism and Numerical Simulation of Pervious Concrete under Salt Freezing-Thawing Cycle

Effects of curing conditions with different temperature and humidity on damage evolution of concrete during freeze–thaw cycling

Relative humidity and deterioration of concrete under freeze–thaw load

The effects of variable-interval reinforcement on academic engagement: a demonstration of matching theory.

Concrete Durability after Load Damage and Salt Freeze-Thaw Cycles