Abstract:ZL205A alloys are prone to generate serious residual stress due to the long solidification intervals and multiphase composition. In this study, the low-pressure casting process for ZL205A alloy hemisphere shell casting was investigated and continuously optimized. In the initial process, the knockout time, pouring temperature, preheating temperature of the sand mould, dwelling pressure, and filling rate were 3 h, 710 degrees C, 30 degrees C, 65 kPa, and 0.33 kPa center dot s(-1), respectively. Macroscopic properties and microstructural features were simulated using a combination of ProCAST and Thermal-Calc software. Additionally, a series of experimental procedures, including EBSD, SEM, EDS, and XRD tests, were conducted to investigate the formation, morphology, and distribution of the microstructure. Current findings demonstrate that during the solidification process, the maximum temperature difference exceeds 220 degrees C, the maximum undercooling reaches 49.56. degrees C, and the maximum effective stress peaks at 301.7 MPa. The residual stress ranges from 20 to 200 MPa. Furthermore, there is no significant texture and preferred grain orientation during nucleation and solidification, and the structure field exhibits an equiaxed crystal but inhomogeneous pattern. Moreover, the finer and more homogeneous the grains and the smaller the deviation in grain orientation, the lower the residual stress. Specifically, two analytical models are developed: one between the casting parameters and the residual stress, and another between the shrinkage defects and the casting parameters. The lowest residual stress is achieved when the knockout time, pouring temperature, pre-heating temperature of the sand mould, dwelling pressure, and filling rate are 6 h, 725 degrees C, 250 degrees C, 95 kPa, and 1.67 kPa center dot s(-1) respectively.

A New Sand Casting Process with Accelerated Solidification Rate

Effects of Hollow Sand Mold on the Microstructure and Mechanical Properties of a Low Pressure Aluminum Alloy Casting

Prediction method of shrinkage cavity and shrinkage porosity in solidification process under low-pressure casting

Cooling Control for Castings by Adopting Skeletal Sand Mold Design

Research on frozen sand mold casting technology for complex thin-walled aluminum alloy castings

Development of Casting Process for Thin Walled Complex-Precision Aluminum Alloy Castings

Effect of freezing range on reducing casting defects through 3D sand-printed mold designs

Chimney Structure of Hollow Sand Mold for Casting Solidification

Determination of casting parameters of thick wall die-casting of magnesium alloy and simulation of its processing

Low Pressure Sand Mould Casting Technology for Heavy Aluminum Alloy Casting

Low-Pressure Casting of Aluminium AlSi7Mg03 (A356) in Sand and Permanent Molds

Optimization of residual stress in low-pressure casting of ZL205A alloys

Additive manufacturing-driven mold design for castings

Effect of Double-Layer-shell Sand Mold on the Residual Stress of Casting and Itself Crack Tendency

Effects of Process Parameters on Internal Quality of Castings During Novel Casting

Modeling and Simulation of the Casting Process with Skeletal Sand Mold

Toward Reducing Casting Defects via 3D Risers via 3D Sand-Printing: A Simulation Study

Optimization of Casting System Structure Based on Genetic Algorithm for A356 Casting Quality Prediction

Digital High-Efficiency Print Forming Method and Device for Multi-Material Casting Molds

Fabrication and posttreatment for inorganic binder jetting sand molds for casting

Mechanism and Application of A Newly Developed Pressure Casting Process: Horizontal Squeeze Casting