Improvement in Surface Performance of Al3ti+Tib2/(Ni Coated Wc) Laser Cladded Coating with Al2o3/Nano-Y2o3

J. N. Li,C. Z. Chen,C. F. Zhang,W. Li
DOI: https://doi.org/10.1179/1433075x11y.0000000008
2011-01-01
Materials Research Innovations
Abstract:Al3Ti+TiB2/(Ni coated WC) laser cladded coating on the Ti-6Al-4V alloy can increase microhardness and wear resistance of the substrate. Nevertheless, due to the actions of a large amount of M6C (Ni2W4C) and the coarse structure, the microhardness of this coating was only 2-3 times higher compared with the substrate. In this study, the Al3Ti+TiB2/(Ni coated WC) +Al2O3/nano-Y2O3 laser cladded coating has been researched by means of X-ray diffraction, scanning electron microscope and energy dispersive spectrometer. The experimental results indicated that with addition of the proper content of Al2O3/nano-Y2O3, the SiO2-Al2O3-Y2O3 system and the Al-Ni-Y amorphous alloy were produced, which were beneficial to increased microhardness and wear resistance of this coating. Furthermore, Al2O3/nano-Y2O3 can also decrease the M6C content, and refine the microstructure of this coating. Accordingly, the microhardness and wear resistance of the Al3Ti+TiB2/(Ni-coated WC) laser cladded coating have been greatly improved.
What problem does this paper attempt to address?