Abstract:A method established in the present study has proven to be effective in the synthesis of Mn2O3 nanocrystals by the thermolysis of manganese(III) acetyl acetonate ([CH3COCH=C(O)CH3](3)-Mn) and Mn3O4 nanocrystals by the thermolysis of manganese(II) acetyl acetonate ([CH3COCH=C(O)-CH3](2)Mn) on a mesoporous silica, SBA-15. In particular, Mn2O3 nanocrystals are the first to be reported to be synthesized on SBA-15. The structure, texture, and electronic properties of nanocomposites were studied using various characterization techniques such as N-2 physisorption, X-ray diffraction (XRD), laser Raman spectroscopy (LRS), temperature-programmed reduction (TPR), transmission electron microscopy (TEM), and X-ray photoelectron spectroscopy (XPS). The results of powder XRD at low angles show that the framework of SBA-15 remains unaffected after generation of the manganese oxide (MnOx) nanoparticles, whereas the pore volume and the surface area of SBA-15 dramatically decreased as indicated by N-2 adsorption-desorption. TEM images reveal that the pores of SBA-15 are progressively blocked with MnOx nanoparticles. The formation of the hausmannite Mn3O4 and bixbyite Mn2O3 structures was clearly confirmed by XRD. The surface structures of MnOx were also determined by LRS, XPS, and TPR. The crystalline phases of MnOx were identified by LRS with corresponding out-of-plane bending and symmetric stretching vibrations of bridging oxygen species (M-O-M) of both MnOx nanoparticles and bulk MnOx. We also observed the terminal Mn=O bonds corresponding to vibrations at 940 and 974 cm(-1) for Mn3O4/SBA-15 and Mn2O3/SBA-15, respectively. These results show that the MnOx species to be highly dispersed inside the channels of SBA-15. The nanostructure of the particles was further identified by the TPR profiles. Furthermore, the chemical states of the surface manganese (Mn) determined by XPS agreed well with the findings of LRS and XRD. These results suggest that the method developed in the present study resulted in the production of MnOx nanoparticles on mesoporous silica SBA-15 by controlling the crystalline phases precisely. The thus-prepared nanocomposites of MnOx showed significant catalytic activity toward CO oxidation below 523 K. In particular, the MnOx prepared from manganese acetyl acetonate showed a higher catalytic reactivity than that prepared from Mn(NO3)(2).

Rapid Synthesis of Cryptomelane-Type Manganese Oxide under Ultrasonic Process

One-pot synthesis of dual-phase manganese dioxide for toluene removal: Effect of crystal phase blending level on oxygen species and activity

A Facile Template-Free Preparation of Porous Manganese Oxides by Thermal Decomposition Method

An ultrasonic atomization assisted synthesis of self-assembled manganese oxide octahedral molecular sieve nanostructures and their application in catalysis and water treatment.

Synthesis, Characterization and Catalytic Combustion Properties of Manganese Oxide Octahedral Molecular Sieve

The Preparation of Cu-Modified Cryptomelane Type-Manganese Oxide Catalysts by one Step sol-gel Synthesis for Decomposition of Methylene Blue

Highly active OMS-2 for catalytic ozone decomposition under humid conditions

Ionic Liquids Assisted Preparation of Manganese Dioxide and Its Catalytic Properties

Monodisperse manganese oxide nanoparticles: Synthesis, characterization, and chemical reactivity

Enhanced catalytic performance by oxygen vacancy and active interface originated from facile reduction of OMS-2

Facile Synthesis Of Amorphous Mesoporous Manganese Oxides For Efficient Catalytic Decomposition Of Ozone

Mesoporous manganese dioxide prepared by nano-casting: An efficient catalyst for of methyl orange and oxalic acid degradation in aqueous solution

Electrode properties of manganese oxide synthesized by sonochemical method in non-aqueous system

Rapid Synthesis of Rod-Like Pyrolucite MnO 2 by Microwave-Assisted Hydrothermal Method

Controlled Synthesis, Characterization, And Catalytic Properties Of Mn2o3 And Mn3o4 Nanoparticles Supported On Mesoporous Silica Sba-15

Study on the mechanism of catalytic oxidative degradation of oxalic acid by two-dimensional (2D) shaped manganese dioxide

Generation of Interfacial High-Spin Manganese Intermediates As Reactive Oxidant During Peroxymonosulfate Activation Mediated by Amorphous MnOx Supported on Polymeric Substrate

Significant Enhancement of Catalytic Activities of Manganese Oxide Octahedral Molecular Sieve by Marginal Amount of Doping Vanadium

Synthesis of mesoporous amorphous MnO2 from SBA-15 via surface modification and ultrasonic waves

Synthesis, characterization, and catalytic activity of cryptomelane nanomaterials produced with industrial manganese sulfate.

Control over the Morphology and Structure of Manganese Oxide by Tuning Reaction Conditions and Catalytic Performance for Formaldehyde Oxidation