Abstract:The combined effects of thermomigration (TM) and electromigration (EM) were investigated in Cu/Sn3.0Ag0.5Cu/Ni solder joints by applying a 5×103A/cm2 DC current to the joints. With a thermal gradient, the Cu atoms and Ni atoms were found to migrate towards the lower temperature side while the Sn atoms were found to migrate towards the higher temperature side. For the solder joint stressed with a 5×103A/cm2 DC current, TM was found to play a dominant effect on the migration of Cu atoms in the solder because the Cu atomic flux in the solder which was induced by EM was smaller than that was induced by TM. The Ni atomic flux in the solder that was induced by TM was smaller than that induced by EM, but it could not be ignored because the values were the same order of magnitude. The Sn atomic flux induced by TM could be ignored due to its smaller magnitude than that induced by EM. The Cu3Sn IMC layer and Cu6Sn5 IMC layer at the Cu/solder interface in the joint with Cu as the anode were thicker than corresponding layers at the Cu/solder interface in the joint with Cu as the cathode. The IMC at the Ni/solder interface of joint with Cu as the anode was the Ni3Sn4 phase while that in the solder joint with Cu as the anode was the (Cu,Ni)6Sn5, and the former was thicker than the latter. EM and TM induced dissolution of the Ni3Sn4 IMC into the solder was found to be the main cause of the formation of voids at the Ni3Sn4/solder interface from a joint that used Cu as the anode. For the solder joint that used Cu as the anode, the Ni3Sn4 IMC layer at the Ni/solder interface was as thick as the Cu-Sn IMC layer at the Cu/solder interface. By contrast, for the solder joint that used Cu as the cathode, the IMC layer at the Ni/solder interface was thinner than that at the Cu/solder interf- - ace.

Electromigration behavior in in-situ Cu6Sn5 reinforced eutectic SnAg composite solder joints

Electromigration in Cu-Cored Sn-3.5Ag-0.7Cu Solder Interconnects under Current Stressing

Electromigration-enhanced intermetallic growth and phase evolution in Cu/Sn–58Bi/Cu solder joints

Electromigration-induced Cracks in Cu/Sn3.5Ag/Cu Solder Reaction Couple at Room Temperature

Electromigration and Thermomigration in Sn3Ag0.5Cu Solder Joints

Retarding Electromigration On The Sn-Ag-Cu Solder Joints By Micro-Sized Metal-Particle Reinforcement

Study Of Em And Tm Of Sn0.3ag0.7cu Solder Joints Under High Current Stress And Thermal Gradient

Study of electromigration in Sn-Ag-Cu micro solder joint with Ni interfacial layer

Electromigration Behaviors in Sb Particle-Reinforced Composite Eutectic Snagcu Solder Joints

Electromigration behavior in Cu/Sn–8Zn–3Bi/Cu solder joint

Effect of electromigration on the tensile strength of Cu/Sn-9Zn/Cu solder interconnects

Effects of Electromigration on the Creep of Sn0.3Ag0.7Cu Solder Joint

Effect of Electromigration of Sn-xAg-Cu Solder Joints on Its Microstructure and Mechanical Properties

Electromigration behavior of Cu-core/Sn-shell solder joints

Investigation of Stress Evolution Induced by Electromigration in Sn-Ag-Cu Solder Joints Based on an X-Ray Diffraction Technique

Electromigration Behavior of Low-Silver Sn-0.3Ag-0.7Cu-1.6Bi-0.2In Solder Joints

Electromigration of SnAgCu Solder Interconnects

Effects of Co Additions on Electromigration Behaviors in Sn–3.0 Ag–0.5 Cu-based Solder Joint

Electromigration-induced failure behavior of low-temperature Cu/Sn-57Bi-1Ag/Cu solder joints

Electromigration and Thermomechanical Fatigue Behavior of Sn0.3Ag0.7Cu Solder Joints

Revealing Evolutions of Intermetallics in a Solder Joint under Electromigration: A Quasi-in Situ Study Combining 3D Microstructural Characterization and Numerical Simulation