Abstract:Highly ordered TiO2 nanotube array electrodes were successfully fabricated by a two-step anodization method on Ti sheet substrates in an electrolyte composed of ammonium fluoride, deionized water, and glycol. The tube wall was smooth, and the average internal and external diameters, wall thickness, and tube length achieved were 80 nm, 90 nm, 10 nm, and 9 μm, respectively. X-ray diffraction and field emission scanning electron microscopy results revealed that the TiO2 nanotube arrays presented an amorphous structure. When calcined at 300 °C, the arrays crystallized into the anatase phase, and the crystallization degree of the oxide layer increased as the temperature rose. Calcinating at 400 °C did not obviously disrupt the porous structure of the highly ordered arrays. However, higher temperature enlarged the diameter of the nanotube array and roughened the tube wall. When the temperature reached 600 °C, the nanotube mouth broke because of the excessive stress, causing the oxide layer’s thinness and nanotube mouth clogging. The photoelectric test showed that the electrode presented obvious photoresponse under 300–400 nm UV excitation (maximized at 360 nm). The degree of crystallization and the micro-structure of the oxide layer can significantly affect the photoelectric properties of the electrode. After calcination at 400 °C, the TiO2 nanotube arrays, with highly ordered tubular structure directly connected to the Ti substrate, can ensure the rapid transportation of photo-induced electrons to the Ti substrate, while the high crystallinity of the arrays can help reduce the defect density of the nanotube and extend the lifetime of the photo-induced carriers. The electrode showed the best photoelectric property, and the photocurrent intensity was maximized (29.6 μA). However, the calcination process with over-temperature resulted in substantial loss of the TiO2 oxide layer, mouth clogging, and a severe decline in the photoelectric properties.

Free-standing TiO2 Nanotube Arrays Fabricated by Anodization

Fabrication of Well-Aligned Tio2 Nanotube Arrays with Outstanding Light-Induced Hydrophilicity Performance

Free-standing TiO(2) nanotube arrays made by anodic oxidation and ultrasonic splitting.

Fabrication of multi-sectional TiO 2 nanotube arrays by anodization

Fabrication and formation mechanism of self-organized TiO2 nanotube arrays

Preparation and Doping of Anodic Tio2 Nanotube Array

Fabrication of Open-Ended Tio2 Nanotube Arrays by A Simple Two-Step Anodization

Study on Fabrication and UV Photoelectric Property of TiO2 Nanotube Array Electrodes.

Fabrication of Titanium Oxide Nanotube Arrays by Anodic Oxidation

Fabrication of TiO2 Nanotube by Electrochemical Anodization: Toward Photocatalytic Application

Tube-In-Tube Tio2 Nanotubes with Porous Walls: Fabrication, Formation Mechanism, and Photocatalytic Properties

TiO2 nanotube arrays prepared by anodic oxidation method

TiO<sub>2</sub> Nanowires/Nanobelts Originating from Anodically Grown Nanotube Arrays

Facile fabrication of open-ended high aspect-ratio anodic TiO 2 nanotube films and their applications

Fabrication of TiO2 Nanotube Arrays on Si Substrates

Synthesis and Photoelectrochemical Properties of Self-Organized Anodic TiO<sub>2</sub> Nanotube Arrays

Aligned metal oxide nanotube arrays: key-aspects of anodic TiO2 nanotube formation and properties

Highly Ordered TiO2 Nanotube Arrays with Engineered Electrochemical Energy Storage Performances

Fabrication of open-ended TiO2 nanotube arrays by anodizing a thermally evaporated Ti/Au bilayer film

Anodization Fabrication of Highly Ordered Tio2 Nanotubes

Synthesis and Photoelectrochemical Properties of Self-Organized Anodic TiO2 Nanotube Arrays