Abstract:Diffusion bonding of additive manufactured (AM) metal parts to traditionally manufactured metal parts could simultaneously achieve large-scale, complex-structure, and multi-material parts. However, there is a lack of study on diffusion bonding as well as its interface formation mechanism between AM metal parts and traditionally manufactured metal parts. In this study, diffusion bonding was performed to join AM 316L stainless steel and casting 45 steel at different temperatures. The element distribution, interface characteristics and shear strength of the joints were investigated, and the interface formation mechanism at different bonding temperature was analyzed in detail. The results reveal that the interface transition zone from the AM 316L steel side to the 45 steel side is composed of the metallic elements diffusion layer and the carbide layer. Moreover, an increase in bonding temperature can effectively promote interface voids closure and increase the thickness of the metallic elements diffusion layer, while the thickness of the carbide layer firstly increases and then decreases as the temperature increases. The component of the carbide layer was identified as brittle compounds (CrFe)23C6 and (CrFe)7C3. The shear strength of the joints exhibited an increasing trend with the increasing bonding temperature. Interestingly, a sudden decrease in strength was found at 950 °C due to the significant increase of the brittle carbide layer, while high-quality joints could be achieved as the brittle carbides dissolve at 1000 °C. This study could lay the foundation for understanding diffusion bonding interface behaviors between AM metal parts and traditional casting metal parts.

Stress Corrosion Behavior of Diffusion Bonding Joints of 316L Stainless Steel in Environment of Acid NaCl Solution

Study on Stress Corrosion Property of 304 Austenitic Stainless Steel in the Environment of Acid Chloride Solution

Interface Evolution Behaviors and Shear Strength of Vacuum Diffusion Bonded 45 Steel/additive Manufactured 316L Stainless Steel Joints

Experimental Investigation of Stress Corrosion Characteristics for 16mnr Steel in Nitrate Solution

Study on Mechanical Properties and Diffusion Bonding Parameters of 316L Stainless Steel

Stress Corrosion Cracking Behavior of Cold-Drawn 316 Austenitic Stainless Steels in Simulated Pwr Environment

Fatigue Damage of Stainless Steel Diffusion-Bonded Joints

Study on stress corrosion behavior of 316L austenitic stainless steel in hot NaOH solution

Environmentally Assisted Cracking of Forged 316LN Stainless Steel and Its Weld in High Temperature Water

Microstructure, Residual Strain and Stress Corrosion Cracking Behavior in 316L Heat-Affected Zone

Interface Behaviors and Mechanical Properties of Diffusion Bonded 45 Steel/additive Manufactured 316L Steel Joints

Stress Corrosion Cracking of 316l Haz for 316l Stainless Steel/Inconel 52m Dissimilar Metal Weld Joint in Simulated Primary Water

Effect of Hydrogen and Stress on Active Dissolution of 304 Stainless Steel in the Environment of Acid NaCl Solution

Microstructure and Mechanical Properties of Diffusion Bonding Joints of 316L Stainless Steel

Interfacial failure mechanism of 316LSS diffusion bonded joints

Towards Understanding Stress Corrosion Cracking of Austenitic Stainless Steels Exposed to Realistic Sea Salt Brines

Stress Corrosion Cracking in the Heat Affected Zone of A Stainless Steel 308L-316L Weld Joint in Primary Water

Mechanical Performances and Failure Modes of Direct Diffusion Bonding Joints of 316L Stainless Steel

Effects of Chloride and Oxygen on Stress Corrosion Cracking of Cold Worked 316/316L Austenitic Stainless Steel in High Temperature Water

Microstructure and Corrosion Behavior of the Heat Affected Zone of a Stainless Steel 308L-316L Weld Joint

Stress Corrosion Cracking Behavior of FV520B Stainless Steel Exposed to Aqueous H2S+Cl-Environment