Mechanical and electrical properties of epoxy resin/epoxidized castor oil/carbon fiber cloth composites
Fan-Long Jin,Heng Zhang,Shan-Shan Yao,Soo-Jin Park
DOI: https://doi.org/10.5714/CL.2017.22.105
2017-01-01
Carbon letters
Abstract:Copyright © Korean Carbon Society http://carbonlett.org Carbon fibers (CFs) have a unique combination of outstanding mechanical, physical, and chemical properties and are among the materials most frequently used in the preparation of a large variety of composites [1-5]. CF-reinforced polymer composites have been widely used in many advanced technological fields, such as aerospace, engineering, sporting goods, automobiles, and marine industry during the past few decades due to their excellent properties, including high strength-to-weight ratios, light weight, high thermal and electrical conductivity, and relative ease of processing [6-10]. However, CFs have poor wettability and adsorption when used with most polymer matrices to make CF-reinforced composites because pristine CFs have chemically inert surfaces and low surface energy. Thus, the properties of the composites are determined not only by the CFs and the polymer matrix, but also by the interface and interphase formed between the two constituents. In general, interfacial adhesion is dominated by the surface properties of CFs (roughness, porosity, functional groups) and the chemical character of the matrix. Favorable interfacial adhesion can efficiently transfer stress from the matrix to the CFs. This plays a major role in determining the mechanical performance and reliability of the composites [11-14]. Various surface modification techniques have been developed to increase the number of surface functional groups and thus enhance the interactions and/or adhesion between the CFs and the matrix. Different surface treatment methods have been used: gas-phase, wet chemical, or electrochemical oxidation, ozone treatment, polymer coating (sizing), and plasma treatment [15-17]. These treatments of CFs improve the interfacial bonding of the final composites to some extent, but unfortunately require high energy consumption. Moreover, during the manufacturing process, commercial CFs are always coated with a sizing layer (epoxy resin) after surface chemical treatment. The epoxy coatings on the surfaces of the CFs are often not removed during the fabrication of CF-reinforced polymer composites. The sizing agents can alter the surface properties of the CFs, as well as their wettability and chemical reactions with the polymer matrix [18-20]. The epoxy matrix in the composite provides bulk and enables the transfer of loads between fibers. The diglycidylether of bisphenol A (DGEBA) is the most commonly used epoxy resin. However, the DGEBA matrix is relatively brittle and has little tensile strength. Therefore, many epoxy resin formulations need to be toughened [21,22]. Thermally latent initiators are inert under normal conditions, i.e., at ambient temperature and light, and become active only under external stimulation such as heating or photoirradiation. Therefore, a thermally latent initiator can easily control the initiation and curing process of an epoxy system, which is desirable for the enhancement of both pot life and handling of epoxy resins [23-26]. In this study, we prepared CF-reinforced epoxy composites using DGEBA as a matrix, epoxidized castor oil (ECO) as a reactive diluent, and carbon fiber cloth (CFC) as a reinforcing agent. We investigated mechanical and electrical properties of the DGEBA/ECO/CFC composites using a universal testing machine, an Izod impact tester, and a direct current (DC) resistance tester. The epoxy resin used in this study was DGEBA (E-51) supplied by Feicheng Deyuan Chemical Co., Ltd. of China, which had an epoxide equivalent weight (EEW) of 185–208 g/ DOI: http://dx.doi.org/ DOI:10.5714/CL.2017.22.105