Tensile impact behaviors and damage mechanism of woven carbon fiber-reinforced-polymer laminates considering adiabatic shear band
Yawei Zhang,Zhiwei Gui,Songyun Ma,Bohua Nan,Shuqiang Xiong
DOI: https://doi.org/10.1016/j.engfailanal.2024.107995
IF: 4
2024-01-29
Engineering Failure Analysis
Abstract:In this study, the tensile impact behavior and damage mechanism of a two-dimensional woven carbon-fiber-reinforced-polymer (CFRP) laminates under different high strain rates are investigated. The damage morphologies are illustrated and studied using meso-macroscale finite element analysis (FEA) and Split Hopkinson bar (SHB) test, FEA results are compared and validated with the SHB test results, and proved to be correct with enough accuracy. The matrix crack first appeared, the tensile stress wave propagated along the interface, which causes shear failure at the interface, which dominated the failure of the specimen and formed adiabatic shear bands inside each ply, the adiabatic shear bands begin to develop in areas with interfacial damage, they are formed after structural damage and propagate in the direction of the interface, accompanied by damage evolution. High strain rate 1400, 1600, and 2400 s −1 impacts tend to lead to direct failure of composite laminates compared to low strain rate 600, and 800 s −1 impacts, the Young's modulus with high strain rate 1400, 1600, and 2400 s −1 are more than twice as much compared to low strain rate 600, and 800 s −1 . The plain-woven CFRP laminates is characterized with strain-rate-hardening effect and strain rate sensitivity, with increase of high strain rate from 600 to 2400 s −1 , the Young's modulus increases from 8.91 to 35.7 GPa, whereas the yield strength increases from 397 to 1298 MPa. The delamination occurs between the plies after crack generation inside the epoxy resin matrix, and begins at a certain strain value after the elastic phase, the micro-cracks propagated along the fiber bundle-matrix interface, thus causing interfacial debonding due to shear stress, these factors result in a strain-rate hardening effect.
engineering, mechanical,materials science, characterization & testing