Abstract:Steel slag can be applied as substitute for natural aggregates in construction applications. The material imposes a high pH (typically 12.5) and low redox potential (Eh), which may lead to environmental problems in specific application scenarios. The aim of this study is to investigate the potential of accelerated steel slag carbonation, at relatively low pCO2 pressure (0.2 bar), to improve the environmental pH and the leaching properties of steel slag, with specific focus on the leaching of vanadium. Carbonation experiments are performed in laboratory columns with steel slag under water-saturated and -unsaturated conditions and temperatures between 5 and 90 °C. Two types of steel slag are tested; free lime containing (K3) slag and K1 slag with a very low free lime content. The fresh and carbonated slag samples are investigated using a combination of leaching experiments, geochemical modelling of leaching mechanisms and microscopic/mineralogical analysis, in order to identify the major processes that control the slag pH and resulting V leaching. The major changes in the amount of sequestered CO2 and the resulting pH reduction occurred within 24h, the free lime containing slag (K3-slag) being more prone to carbonation than the slag with lower free lime content (K1-slag). While carbonation at these conditions was found to occur predominantly at the surface of the slag grains, the formation of cracks was observed in carbonated K3 slag, suggesting that free lime in the interior of slag grains had also reacted. The pH of the K3 slag (originally pH±12.5) was reduced by about 1.5 units, while the K1 slag showed a smaller decrease in pH from about 11.7 to 11.1. However, the pH reduction after carbonation of the K3 slag was observed to lead to an increased V-leaching. Vanadium leaching from the K1 slag resulted in levels above the limit values of the Dutch Soil Quality Decree, for both the untreated and carbonated slag. V-leaching from the carbonated K3 slag remained below these limit values at the relatively high pH that remained after carbonation. The V-bearing di-Ca silicate (C2S) phase has been identified as the major source of the V-leaching. It is shown that the dissolution of this mineral is limited in fresh steel slag, but strongly enhanced by carbonation, which causes the observed enhanced release of V from the K3 slag. The obtained insights in the mineral transformation reactions and their effect on pH and V-leaching provide guidance for further improvement of an accelerated carbonation technology.

Pore Structural Changes and Carbonated Depth of Carbonated Steel Slag

Analysis of Mechanical Performance and Microstructure of Steel Slag Processed with Accelerated Carbonation

Effect of Carbonation Treatment on the Properties of Steel Slag Aggregate

Effect of CO2 treatment on the microstructure and properties of steel slag supplementary cementitous materials

A Review on the Carbonation of Steel Slag: Properties, Mechanism, and Application

Interdependent factors contributing towards carbonation of steel slag compact: consideration of casting pressure, water dosage and carbonation duration

Impacts of Hydration Degree of Steel Slag on Its Subsequent CO2 Capture Behaviors and Mechanical Performances of Prepared Building Materials

Accelerated carbonation of steel slag: A review of methods, mechanisms and influencing factors

Utilization of accelerated carbonation to enhance the application of steel slag: a review

Accelerated carbonation of steel slag monoliths at low CO2 pressure – microstructure and strength development

Effects of carbonation degree on the hydration reactivity of steel slag in cement-based materials

Probe into carbonation mechanism of steel slag via FIB-TEM: The roles of various mineral phases

Changes in mineralogical and leaching properties of converter steel slag resulting from accelerated carbonation at low CO2 pressure

Evaluation of Potential Factors Affecting Steel Slag Carbonation

Use of steel slag as carbonation material: A review of carbonation methods and evaluation, environmental factors and carbon conversion process

In-situ investigation on the carbonation behaviors of various mineral phases in steel slag: The role of RO phase

Carbon sequestration of steel slag and carbonation for activating RO phase

Development of high-volume steel slag as cementitious material by ethylenediamine tetraacetic acid induced accelerated carbonation

Enhanced Steelmaking Slag Mineral Carbonation in Dilute Alkali Solution

A review of use of metallurgical slag for its carbonation products: processes, crystallization behavior, and application status

Analysis of Hydration Mechanism of Steel Slag-Based Cementitious Materials under Saline–Alkaline-Coupled Excitation