Accelerated carbonation of steel slag monoliths at low CO2 pressure – microstructure and strength development

P. Nielsen,M.A. Boone,L. Horckmans,R. Snellings,M. Quaghebeur

DOI: https://doi.org/10.1016/j.jcou.2019.10.022

IF: 7.7

2020-02-01

Journal of CO2 Utilization

Abstract:Several studies have focused on the parameters that influence the CO2-uptake of steel slags during mineral carbonation, however, less is known about the parameters that affect the strength development of the carbonated products. In this study monoliths with a compressive strength of 30–50 MPa were made by mineral carbonation of compacted stainless steel slag in an autoclave under mild operating conditions (i.e. 10–60 °C, 1.5 bar P total, and 5–100 % CO2). The influence of moisture content, CO2 concentration, temperature and exposure time on CO2 uptake and strength development were evaluated.In general a good correlation was observed between CO2 uptake and compressive strength of the monoliths. At different temperatures however the compressive strength as a function of CO2 uptake differed. The highest CO2 uptake was realized for carbonation at 60°, the resulting compressive strength however is lower than for experiments carried out at lower temperature.The microstructure indicated a difference in carbonate precipitation between the samples carbonated at different temperatures. In the samples carbonated at 10 and 20 °C the carbonate crystals mainly precipitated on the slag particle surfaces and at particle contacts, strengthening the particle packing of the compacts. At 60 °C carbonate crystals did initially not precipitate on particle surfaces, but most likely at the fluid-gas interfaces, which resulted in a different microstructure and lower compressive strengths for an equivalent CO2 uptake.

engineering, chemical,chemistry, multidisciplinary