Abstract:Kaolinite-urea intercalation complex was prepared using kaolinite as intercalation host and urea as intercalating agent. The kaolinite-urea intercalation complex was used as precursor to prepare exfoliated kaolinite by deintercalating urea molecules from the interlayers of kaolinite through ultrasonic treatment. X-ray diffraction (XRD) and scanning electron microscopy (SEM) were used to characterize the as-prepared exfoliated kaolinite. A broad 001 diffraction of kaolinite with weak intensity showed the random orientation of kaolinite platelets. SEM micrograph confirmed the exfoliation of kaolinite particles with layer thickness of no more than 50 nm. The exfoliated kaolinite particles were used as filler to poly(ethylene-oxide)/LiClO4 (PEO/LiClO4) system to prepare PEO/kaolinite composites, with the aim to improve the ion conductivity and mechanical property of the PEO matrix. SEM, transmission electron microscopy (TEM), XRD and Fourier transform infrared spectroscopy (FTIR) were used to characterize the PEO/kaolinite composites. SEM and TEM micrographs exhibited a good dispersion of exfoliated kaolinite in PEO matrix. XRD results showed that the crystallinity of PEO was gradually decreasing with increased exfoliated kaolinite content. FTIR analysis indicated that the hydrogen bonding was formed between the oxygen atoms of PEO segments and the hydroxyl groups on kaolinite surface, and this interaction between PEO and kaolinite was beneficial to the decrease in crystallinity of PEO. In order to evaluate the effect of the exfoliated kaolinite on ion conductivity and mechanical property of PEO matrix, AC impedance measurement and mechanical test were carried out. The results indicated that the ion conductivity of the composites gradually increased with increased exfoliated kaolinite content and reached 6.0 x 10(-5) S/cm at filler concentration of 20 wt%. The formation of amorphous region around the exfoliated kaolinite was beneficial for the Li+ ion conduction in PEO matrix. When the exfoliated kaolinite content reached 10 wt%, the formed amorphous regions were connected to each other to form a network for the transport of Li+ in the interconnected amorphous regions, leading to a sharp increase in ion conductivity. Moreover, the prepared composites under different drying temperature exhibited different ion conductivity. The reason was attributed to the change of PEO crystallinity with drying temperature, and the change trend of the ion conductivity was consistent with that of PEO crystallinity. Under the drying temperature of 95 degrees C, the as-prepared composite possessed high ion conductivity (6.8 x 10(-5) S/cm). In addition, the Young's modulus and tensile strength of the composites were improved because of the introduction of the exfoliated kaolinite into EPO matrix. The composites showed the maximal increase of 256% and 121% in Young's modulus and tensile strength, i.e., to 165.1 MPa and 6.743 MPa respectively, compared to PEO/LiClO4 (46.3 and 3.047 MPa). Therefore, the exfoliated kaolinite was a promising filler to prepare PEO based polymer electrolyte.

Effect of electrical characteristics modification on viscosity of kaolin suspension

Research on dispersion characteristics of micron grade Al_2O_3 particle in water phase

Effect of Sequentially Adsorbed Multilayers, Citric Acid(ca)-Pei-ca-pei and PEI-CA-PEI-CA, on the Surface Chemistry and Rheology of Spherical Α-Alumina Suspensions

Effect of Dispersants Pre-Adsorption and Grinding on Dispersion Performance of Kaolin Pigment

Effect of Clay Minerals on Pulp Rheology and the Flotation of Copper and Gold Minerals

Facile One-Step Microwave-Assisted Modification of Kaolinite and Performance Evaluation of Pickering Emulsion Stabilization for Oil Recovery Application.

Effect of Electrolytes on Interactions Between a Novel Organic-Inorganic Hybrid Polymer Flocculant and Kaolinite Particles

The effect of polymer and surfactant adsorption on the colloidal stability and rheology of kaolin dispersions

Effects of Humic Acid on Physical and Hydrodynamic Properties of Kaolin Flocs by Particle Image Velocimetry

The key role of the polycation in the mechanical resistance of wet kaolinite modified with interpolyelectrolyte complexes

Preparation and Characterization of Poly(ethylene-oxide)/Kaolinite Composite Electrolyte

Mechanistic Links Between Magnetic Nanoparticles and Recovery Potential and Enhanced Capacity for Crystal Violet of Nanoparticles-Coated Kaolin

Comparative study on the effectiveness of hydrophobically modified cationic polyacrylamide groups in the flocculation of kaolin

Effects of Magnesium Electrolyte on Rheological Properties of Alumina Slurry

Experimental study of the effects of soil pH and ionic species on the electro-osmotic consolidation of kaolin.

Effects of anionic additives on the rheological behavior of aqueous calcium montmorillonite suspensions

Effect of solution pH and polyethylene oxide concentration on surface/interface properties, flocculation and rheology of concentrated monodisperse ultrafine synthetic tailings slurry

Study on the dispersion stability of kaolin in oil phase

Study On The Rheological Behavior Of Sub-Micron Alumina Aqueous Suspensions

Interaction between PEO and Kaolinite in Flocculating: An Experimental and Molecular-Simulation Study

Ph Effects on Shear Thickening Behaviors of Polystyrene-Ethylacrylate Colloidal Dispersions