Abstract:Kaolinite-urea intercalation complex was prepared using kaolinite as intercalation host and urea as intercalating agent. The kaolinite-urea intercalation complex was used as precursor to prepare exfoliated kaolinite by deintercalating urea molecules from the interlayers of kaolinite through ultrasonic treatment. X-ray diffraction (XRD) and scanning electron microscopy (SEM) were used to characterize the as-prepared exfoliated kaolinite. A broad 001 diffraction of kaolinite with weak intensity showed the random orientation of kaolinite platelets. SEM micrograph confirmed the exfoliation of kaolinite particles with layer thickness of no more than 50 nm. The exfoliated kaolinite particles were used as filler to poly(ethylene-oxide)/LiClO4 (PEO/LiClO4) system to prepare PEO/kaolinite composites, with the aim to improve the ion conductivity and mechanical property of the PEO matrix. SEM, transmission electron microscopy (TEM), XRD and Fourier transform infrared spectroscopy (FTIR) were used to characterize the PEO/kaolinite composites. SEM and TEM micrographs exhibited a good dispersion of exfoliated kaolinite in PEO matrix. XRD results showed that the crystallinity of PEO was gradually decreasing with increased exfoliated kaolinite content. FTIR analysis indicated that the hydrogen bonding was formed between the oxygen atoms of PEO segments and the hydroxyl groups on kaolinite surface, and this interaction between PEO and kaolinite was beneficial to the decrease in crystallinity of PEO. In order to evaluate the effect of the exfoliated kaolinite on ion conductivity and mechanical property of PEO matrix, AC impedance measurement and mechanical test were carried out. The results indicated that the ion conductivity of the composites gradually increased with increased exfoliated kaolinite content and reached 6.0 x 10(-5) S/cm at filler concentration of 20 wt%. The formation of amorphous region around the exfoliated kaolinite was beneficial for the Li+ ion conduction in PEO matrix. When the exfoliated kaolinite content reached 10 wt%, the formed amorphous regions were connected to each other to form a network for the transport of Li+ in the interconnected amorphous regions, leading to a sharp increase in ion conductivity. Moreover, the prepared composites under different drying temperature exhibited different ion conductivity. The reason was attributed to the change of PEO crystallinity with drying temperature, and the change trend of the ion conductivity was consistent with that of PEO crystallinity. Under the drying temperature of 95 degrees C, the as-prepared composite possessed high ion conductivity (6.8 x 10(-5) S/cm). In addition, the Young's modulus and tensile strength of the composites were improved because of the introduction of the exfoliated kaolinite into EPO matrix. The composites showed the maximal increase of 256% and 121% in Young's modulus and tensile strength, i.e., to 165.1 MPa and 6.743 MPa respectively, compared to PEO/LiClO4 (46.3 and 3.047 MPa). Therefore, the exfoliated kaolinite was a promising filler to prepare PEO based polymer electrolyte.

The key role of the polycation in the mechanical resistance of wet kaolinite modified with interpolyelectrolyte complexes

Hydraulic performance of activated calcium bentonite treated by polyionic charged polymer

The Role of Exfoliated Kaolinite on Crystallinity, Ion Conductivity, Thermal and Mechanical Properties of Poly(ethylene Oxide)/kaolinite Composites

Na-CMC-amended clay: effect of mixing method on hydraulic conductivity and polymer elution

Understanding Cationic Polymer Adsorption on Mineral Surfaces: Kaolinite in Cement Aggregates

Effect of Electrolytes on Interactions Between a Novel Organic-Inorganic Hybrid Polymer Flocculant and Kaolinite Particles

Preparation and Characterization of Poly(ethylene-oxide)/Kaolinite Composite Electrolyte

Effects of Biopolymers on the Liquid Limit and Undrained Shear Strength of Soft Clays

Dynamics of Water Intrusion in Polyelectrolyte-Bound Kaolinite: An Insight into Durability Mechanisms via Atomistic Modeling

Study on Preparation of Polymer-Modified Bentonite and Sand Mixtures Based on Osmotic Pressure Principle

Experimental Study on the Mechanical Properties and Microstructure of Metakaolin-Based Geopolymer Modified Clay

Polymer Treatment of Bentonite Clay for Contaminant Resistant Barriers

Characterisation of bentonite polymer for bottom liner use

The effect of polymer and surfactant adsorption on the colloidal stability and rheology of kaolin dispersions

Performance of eco-friendly polymers for soil stabilization and their resistance to freeze–thaw action

Pore-scale mechanisms underlying the behavior of enhanced bentonites exposed to aggressive inorganic solutions

Polymer-treated bentonite clay for chemical-resistant geosynthetic clay liners

Polymer Fouling and Hydraulic Conductivity of Mixtures of Sodium Bentonite and a Bentonite-Polymer Composite

Consolidation and swelling behavior of kaolinite clay containing xanthan gum biopolymer

Novel composite polymer-amended bentonite for environmental containment: Hydraulic conductivity, chemical compatibility, enhanced rheology and polymer stability

Rheological Behavior of Clay Tailings in the Presence of Divalent Cations and Sodium Polyacrylate: Insights from Molecular Dynamics Simulations