Abstract:Highly oriented titania nanotube (TN) arrays with {1 0 1} crystal face were prepared on the surface of titanium substrate by liquid chemical deposition method. The obtained titania samples were characterized by X-ray diffraction (XRD), atomic force microscope (AFM), scanning electron microscope (SEM), BET measurements, diffuse reflectance spectroscopy (DRS), and electron paramagnetic resonance (EPR) spin trap technique. Results indicate that the nanotubes grown in this study are well-aligned and organized into high-density uniform arrays. The typical dimensions of the hollow tube are ∼90 nm in outer diameter, ∼60 nm in inner diameter, ∼15 nm in wall thickness and ∼300 nm in height. The BET surface area of the obtained titania nanotube is 275 m2/g. The EPR signals reveal that hydroxyl radical (OH) species can be produced in the nanotube system, and no OH radical EPR signals were detected under dark and/or nanotube non-existing situations. The catalytic degradation of a textile azo dye, acid orange 7 (AO7), in aqueous solution with titania nanotube arrays electrode was carried out using photo-electrocatalytic (PEC) process, comparing with electrochemical process (EP) and photocatalytic (PC) process. A significant photo-electrochemical synergetic effect was observed, which is due to the efficient charge separation and transfer at the surface-interface of titania nanotube arrays. The kinetic constant of PEC degradation of AO7 using TN electrode was 48.7%, which is higher than that using P-25 TiO2 film and TiO2 particular film electrode. The enhanced degradation rate of AO7 using titania nanotube arrays could be attributed to their larger specific surface area and nanotubular structure with preferred reactive crystal face, which would increase their absorption capacity to the targeted substrates and the rate of surface-interface charge transfers in titania nanotube semiconductor redox systems.

Enhanced Photoelectrocatalytic Degradation of Azo-Dye Pollutants Using Transparent Titania Nanotube Arrays Glass Electrode

Enhanced Visible-Light-Induced Photoelectrocatalytic Degradation of Methyl Orange by Cds Sensitized Tio2 Nanotube Arrays Electrode

Electrochromic Titania Nanotube Arrays for the Enhanced Photocatalytic Degradation of Phenol and Pharmaceutical Compounds

Fabrication and Photo-Electrocatalytic Properties of Highly Oriented Titania Nanotube Arrays with {1 0 1} Crystal Face

Fabrication and photo-electrocatalytic properties of highly oriented titania nanotube arrays with {1 0 1} crystal face

Fabrication of Fe2O3/TiO2 Nanotube Electrode and Its Photoelectrocatalytic Performance in Dye Wastewater Degradation

Fabrication of Fe 2 O 3 /TiO 2 Nanotube Electrode and Its Photoelectrocatalytic Performance in Dye Wastewater Degradation: Fabrication of Fe 2 O 3 /TiO 2 Nanotube Electrode and Its Photoelectrocatalytic Performance in Dye Wastewater Degradation

Highly-ordered Dye-Sensitized TiO 2 Nanotube Arrays Film Used for Improving Photoelectrochemical Electrodes

Fabrication of Fe<SUB>2</SUB>O<SUB>3</SUB>/TiO<SUB>2</SUB> Nanotube Electrode and Its Photoelectrocatalytic Performance in Dye Wastewater Degradation

Photoelectrochemical Degradation of Methyl Orange by TiO2 Nanopore Arrays Electrode and Its Comparison with TiO2 Nanotube Arrays Electrode

Photoelectrocatalytic activity of highly ordered TiO2 nanotube arrays electrode for azo dye degradation

Defective TiO2 Nanotube Arrays for Efficient Photoelectrochemical Degradation of Organic Pollutants

Synthesis of α-Fe2O3/TiO2 nanotube arrays for photoelectro-Fenton degradation of phenol

Electrochemically Reduced Phytic Acid-Doped TiO2 Nanotubes for the Efficient Electrochemical Degradation of Toxic Pollutants.

Fabrication of MnO2/TiO2 nano-tube arrays photoelectrode and its enhanced visible light photoelectrocatalytic performance and mechanism

Single-crystalline Rutile TiO2 Nanorod Array on Flexible Ti Substrates for Efficient Photoelectrocatalytic Degradation of Phenol in Water

Green Synthesized Palladium Coated Titanium Nanotube Arrays for Simultaneous Azo-Dye Degradation and Hydrogen Production

Preparation of short, robust and highly ordered TiO2 nanotube arrays and their applications as electrode

3D-TNAs composite electrodes with enhanced visible-light photoelectrocatalytic performance and stability

Photocatalytic degradation of methyl orange using a TiO2/Ti mesh electrode with 3D nanotube arrays.

Fabrication and Photoelectrochemical Properties of Highly Ordered TiO_2 Nanotube Arrays on Glass Substrate