Abstract:Highly oriented titania nanotube (TN) arrays with {1 0 1} crystal face were prepared on the surface of titanium substrate by liquid chemical deposition method. The obtained titania samples were characterized by X-ray diffraction (XRD), atomic force microscope (AFM), scanning electron microscope (SEM), BET measurements, diffuse reflectance spectroscopy (DRS), and electron paramagnetic resonance (EPR) spin trap technique. Results indicate that the nanotubes grown in this study are well-aligned and organized into high-density uniform arrays. The typical dimensions of the hollow tube are ∼90 nm in outer diameter, ∼60 nm in inner diameter, ∼15 nm in wall thickness and ∼300 nm in height. The BET surface area of the obtained titania nanotube is 275 m2/g. The EPR signals reveal that hydroxyl radical (OH) species can be produced in the nanotube system, and no OH radical EPR signals were detected under dark and/or nanotube non-existing situations. The catalytic degradation of a textile azo dye, acid orange 7 (AO7), in aqueous solution with titania nanotube arrays electrode was carried out using photo-electrocatalytic (PEC) process, comparing with electrochemical process (EP) and photocatalytic (PC) process. A significant photo-electrochemical synergetic effect was observed, which is due to the efficient charge separation and transfer at the surface-interface of titania nanotube arrays. The kinetic constant of PEC degradation of AO7 using TN electrode was 48.7%, which is higher than that using P-25 TiO2 film and TiO2 particular film electrode. The enhanced degradation rate of AO7 using titania nanotube arrays could be attributed to their larger specific surface area and nanotubular structure with preferred reactive crystal face, which would increase their absorption capacity to the targeted substrates and the rate of surface-interface charge transfers in titania nanotube semiconductor redox systems.

Green Synthesized Palladium Coated Titanium Nanotube Arrays for Simultaneous Azo-Dye Degradation and Hydrogen Production

Hydrothermal Growth of Nanorod Arrays and in Situ Conversion to Nanotube Arrays for Highly Efficient Ag-sensitized Photocatalyst

Ag Plasmonic Enhancement of Visible-Light Photoelectrocatalytic Activity for Defect-Sensitized TiO2 Nanotube Arrays

Single-crystalline Rutile TiO2 Nanorod Array on Flexible Ti Substrates for Efficient Photoelectrocatalytic Degradation of Phenol in Water

Defective TiO2 Nanotube Arrays for Efficient Photoelectrochemical Degradation of Organic Pollutants

A Visible Light Responsive Photocatalytic Fuel Cell Using BiOBr/TiO2 Nanotube Array Photoanode for Simultaneous Wastewater Treatment and Electricity Generation

Synthesis of Co3O4/Ag/TiO2 Nanotubes Arrays Via Photo-Deposition of Ag and Modification of Co3O4 (311) for Enhancement of Visible-Light Photoelectrochemical Performance

Electrochemically Reduced Phytic Acid-Doped TiO2 Nanotubes for the Efficient Electrochemical Degradation of Toxic Pollutants.

Fabrication of MnO2/TiO2 nano-tube arrays photoelectrode and its enhanced visible light photoelectrocatalytic performance and mechanism

Ta-Doped Porous TiO2 Nanorod Arrays by Substrate-Assisted Synthesis: Efficient Photoelectrocatalysts for Water Oxidation

Energy band and interface engineering of ternary TNAs/g-C 3 N 4 /NCQDs photoanode with enhanced optical absorption and charge transfer for efficient photoelectrochemical water oxidation

Preparation of short, robust and highly ordered TiO2 nanotube arrays and their applications as electrode

3D-TNAs composite electrodes with enhanced visible-light photoelectrocatalytic performance and stability

Fabrication and photo-electrocatalytic properties of highly oriented titania nanotube arrays with {1 0 1} crystal face

Fabrication and Photo-Electrocatalytic Properties of Highly Oriented Titania Nanotube Arrays with {1 0 1} Crystal Face

A Facile Strategy to Synthesize Pd/TiO2 Nanotube Arrays with High Visible Light Photocatalytic Performance

Photoelectrochemical oxidation of azo dye and generation of hydrogen via C N co-doped TiO 2 nanotube arrays

Synergistic mechanism of B doping and NiO loading on the excellent PEC performance and high stability of TiO 2 nanotube photoanodes

Enhanced Visible Light Photoelectrochemical Performances with Nitrogen Doped TiO_2 Nanowire Arrays

Efficient photoelectrocatalytic degradation of tylosin on TiO2 nanotube arrays with tunable phosphorus dopants

Controllable Synthesis of Well-Ordered TiO2 Nanotubes in a Mixed Organic Electrolyte for High-Efficiency Photocatalysis