Abstract:The aim of this study is to correlate the solubility and electrospinnability of gelatin in different organic solvent systems. Teas graph was employed using the Hansen parameters in this systematic study to map the solvents that dissolve and enable the electrospinning of gelatin. It was found that in some cases, the solvent dissolved gelatin but the solution was not spinnable. Increasing the hydrogen bonding force ( f h ) assisted in the electrospinning of the gelatin solution. Higher dispersion force ( f d ) improves the electrospinnability at lower concentration of gelatin. The viscosity of the solution of pure acetic acid (AA) is higher than the binary solution of 3:1 AA/water and 3:1 AA/tetrahydrofuran (THF) for the same concentration of gelatin; the higher viscosity enhanced the electrospinning properties. Interestingly, field-emission scanning electron microscopy arrayed that the effect of increasing the concentration of gelatin in the pure AA system resulted in the formation of thicker fibres, however, it induced the formation of uniform fibres in the 3:1 AA/water system, whereas beaded morphology was obtained when lower concentration of gelatin was used. The fibres obtained from electrospinning the solution of 3:1 AA/THF resulted in the formation of thicker and non-uniform fibres due to the low electrical conductivity as well as the high volatility of the solution. Attenuated total reflectance-Fourier transform infrared spectroscopy portrayed all the major peaks of gelatin in the electrospun fibres. However, widening of the Amide-A peak of gelatin was observed when the solvent system of formic acid and 3:1 AA/THF were used. Thermal study of the fibre mats depicts that the binary solvent system using AA is more suitable to obtain nanofibres with more analogous structure to pristine gelatin. The electrospun samples of gelatin in the different solvent systems did not exhibit any cytotoxity on the HeLa cell line. Teas graph can be used as a quick solvent selection tool to prepare electrospinning solutions of gelatin blended with synthetic polymers to obtain nanofibres for biomedical applications.

Electrospinnability of Gelatin Aqueous Solution with the Addition of Sodium Docecyl Sulfate and Ethanol

Effect On The Electrospinnability By Adding Surfactant In Gelatin Aqueous Solution

Precise Printing of Microfiber Scaffold with Gelatin Methacryloyl (gelma)/polyethylene Oxide (PEO) Bioink

Effects of Various Surfactants on Alkali Lignin Electrospinning Ability and Spun Fibers

Influence of SDS and ethanol on forming process of gelatin ultrafine fiber

Electrospinning and mechanical characterization of gelatin nanofibers

Electrostatic Spinning of Aqueous Gelatin Solution

Comparison of Ethyl Cellulose-Gelatin Composite Films Fabricated by Electrospinning Versus Solvent Casting

STUDIES ON ONE-STEP ELECTROSPINNING FOR PREPARING CROSSLINKED GELATIN FIBERS

Electrospinning of Poly(Vinyl Alcoh01)/Gelatin Aqueous Solution

Understanding the solubility and electrospinnability of gelatin using Teas approach in single/binary organic solvent systems

Development of Hybrid Electrospun Nanofibers: Improving Effects of Cellulose Nanofibers (CNFs) on Electrospinnability of Gelatin

Preparation of electrospun nanofibers from solutions of different gelatin types using a benign solvent mixture composed of water/PBS/ethanol

Study on Processing of Gelatin Ultrafine Fibers

Fabrication of gelatin nanofibrous scaffolds using ethanol/phosphate buffer saline as a benign solvent.

Research Progress in Electrospinning of Gelatin Micrometer and Nano Scale Fibers

Tunable Physical Properties of Ethylcellulose/Gelatin Composite Nanofibers by Electrospinning

Electrospinning of Gelatin Fibers and Gelatin/Pcl Composite Fibrous Scaffolds

Study on Wettability, Mechanical Property and Biocompatibility of Electrospun Gelatin/zein Nanofibers Cross-Linked by Glucose

Electrospinning of Silver/Sodium Alginate/Poly(vinyl Alcohol) Fibers

Characterization of Gelatin/zein Nanofibers by Hybrid Electrospinning