Abstract:Water is a good solvent for the gelatin nanofibers prepared by electrospinning process, but the spinning temperature must be maintained around 60 degrees C to 65 degrees C. Gelatin mats with ultrafine fibers varied from 178 rim to 267 run can be prepared under the optimized electrospinning conditions when the concentration varied from 15 wt % to 25 wt %. Beads is evidence in regular arrays along ultrafibers when the gelatin concentration was below 15 w t %. Sodium dodecyl sulfate (SDS) was added to improve the electrospinnability of the gelatin solution of 13 wt %t. It has been recognized that the surface tension of gelatin aqueous solution was decreased when SDS was added, meanwhile the conductivity and the viscosity increased. With the SDS content of 0.3 wt % and 0.5 wt %, beads along the gelatin fibers vanished. Smooth and uniform ultrafine gelatin fibers with fibers' diameter 153 nm and 132 nm were obtained.

Effect On The Electrospinnability By Adding Surfactant In Gelatin Aqueous Solution