Microstructures and Mechanical Properties of Alloys Co-9Al-(9-x)W-xMo-2Ta-0.02B at Room and High Temperatures

Hao LI,Jiangbo SHA,Shusuo LI
2011-01-01
Abstract:Based on the composition of Co-9Al-9W-2Ta-0.02B,2at%,4at%,6at% and 9at% Mo are added to replace W(hereafter referred to as alloys 2Mo,4Mo,6Mo and 9Mo respectively;Mo-free alloy is referred to as alloy 0Mo).The effect of Mo additions on phase constitution,microstructure,HV hardness and room/high-temperature strength is investigated.It is found that the as-cast alloys show a microstructure composed of Co-base solid solution γ phase and intermetallic Co3(Al,Me) compound γ′ phase(where Me stands for W,Mo and Ta).The γ phase is the matrix and the γ′ phase is distributed on the grain boundaries of the γ phase.After 1 350 ℃/8 h solution and 800 ℃/100 h aging,a cubic γ′ phase with a size of 200-300 nm homogeneously precipitates in the γ matrix for alloys 0Mo,2Mo and 4Mo,and the as-cast γ′ phase disappears.As for alloys 6Mo and 9Mo,the microstructure is significantly changed;however,no cubic γ′ precipitates are found in the γ matrix;instead there is a large number of needle-like TCP precipitates,while the as-cast γ′ phase Co3(Al,Me) compound changes to Co3(Al,Mo) compound.Abnormal yield characteristic is found for all alloys.As the Mo content increases,the room/high-temperature strength of the heat-treated alloys decreases,and the abnormal yield temperature shifts towards lower temperatures.
What problem does this paper attempt to address?