Microstructural Characteristics of Directionally Solidified Ni-43ti-4al-2nb-2hf Alloy

Yurong Sang,Lijing Zheng,Qing Pan,Lei Zhou,Yan Li,Hu Zhang
DOI: https://doi.org/10.1007/s12598-011-0299-0
2011-01-01
Abstract:By liquid metal cooling (LMC) process, the Ni-43Ti-4Al-2Nb-2Hf (atomic fraction, %) alloy was directionally solidified (DS) at different casting temperatures (1350, 1450, 1550 °C) and a constant withdrawal rate of 6mm/min. Compared to the as-cast alloy, DS process has no effect on the phase composition, but significantly influences the phase morphologies. After DS, the NiTi phase preferentially grows along [100] orientation, and the macrostructure becomes the columnar crystals morphology with the [100] growth direction. Owing to the micro-segregation difference of Nb and Hf, the contrasts of primary NiTi phase become lighter from the center of dendrites to the edge. White Nb-rich Ti 2 Ni phases distribute along growth direction in the light-contrast interdendritic regions, accompanied by Ti 2 Ni precipitates. Actually, the finally solidified Ti 2 Ni phase is the quasi-eutectic structure composed of Nb-rich Ti 2 Ni and Ti 2 Ni phase. The increases of casting temperature make the dendrites finer, also, Nb-rich Ti 2 Ni more dispersively distributed.
What problem does this paper attempt to address?