Abstract:A variety of HZSM-5 zeolites with different b-axis thicknesses and SiO2/Al2O3 were fabricated by simply modifying urea content and Al source feeding in the initial gel, respectively. Multiple characterization technologies including XRD, SEM, N-2 adsorption-desorption, NH3-TPD and Py-IR were employed to investigate physicochemical properties of these samples and the possible crystallization mechanism was proposed that adsorption of urea molecules on (010) facet was the key factor for fabricating thin-sheet HZSM-5 zeolites. The results of hexane cracking reaction revealed that the selectivities of light olefins reached 46.5% when controlling b-axis thickness to 340 nm, exceeding the control sample by 12.2%. Furthermore, the effect of SiO2/Al2O3 under this b-axis thickness was also investigated and concluded that keeping SiO2/Al2O3 to 200 could exhibit the optimum catalytic performance with the conversion of 95.5% and light olefins selectivities of 56.7%. The reaction conditions were optimized to be 600 degrees C at the N-2 flow rate of 25 mL/min and WHSV of 3 h(-1) to arouse the best performance. Under this condition, the distribution of ethene and propene was quite close to that of thermodynamic equilibrium. Based on these results, the primary and secondary products were uncovered, and further the reaction pathway of hexane cracking was disclosed. This new strategy to synthesize sheet-like catalysts for enhancing the catalytic properties in hexane cracking also laid a solid foundation for the study of the catalysts on light oil cracking in industry.

Study on Process of Cyclohexene Hydration over Solid Zeolite

HZSM-5 zeolite modification and catalytic reaction mechanism in the reaction of cyclohexene hydration

Optimization of Cyclohexanol Synthesis from Hydration of Cyclohexene

The Adsorption and Catalytic Cracking of C8 Hydrocarbons on HZSM-5 Zeolite

Amphiphilic HZSM-5 Zeolite Catalyst for Hydration of Cyclohexene on Phase-boundary Interface

A Study of ZSM-5 Molecular Sieve Shaping for an Innovative Cyclohexene Hydration Process

Amphiphilic HZSM-5 for Cyclopentene Hydration at the Liquid–Liquid Interface in Pickering Emulsion

Studing on Prepration of Cyclohexene by Various Catalysts

Synthesis of Hierarchical ZSM‐11 Nanorods Aggregates and Catalytic Properties in Cyclohexene Hydration to Cyclohexanol

Solvent Effects on Hydration of Cyclohexene over H-Zsm-5 Catalyst

Promotion of Ultrasound on Cyclohexene Hydration over HZSM-5 Catalyst

Synthesis of HZSM-5 Catalyst by Template-Free Method for Hydration of Cyclohexene to Cyclohexanol

Preparation and Characterization of Amphiphilic HZSM-5 Zeolite with Various Si/Al Ratios

Effects of post treatment of HZSM-5 zeolites on catalytic cracking of butene

Fabrication of Sheet-Like HZSM-5 Zeolites with Various SiO2/Al2O3 and Process Optimization in Hexane Catalytic Cracking

Optimization of Conditions for Preparation of ZSM-5@silicalite-1 Core–shell Catalysts Via Hydrothermal Synthesis

Synergism Between the Lewis and Brönsted Acid Sites on HZSM-5 Zeolites in the Conversion of Methylcyclohexane

Research progress in cyclohexene hydration to cyclohexanol

Stability of Zeolite HZSM-5 in Liquid Phase Dehydration of Methanol to Dimethyl Ether

Acid treatment to adjust zeolite hydrophobicity for olefin hydration reaction

Study on the Conversion of Methanol to Olefins over ZSM-5