Abstract:Hexadecyltrimethylammonium bromide (CTAB) was utilized to template the growth of mesoporous silica particles via ammonia-catalyzed hydrolysis and condensation of tetraethoxysilane (TEOS) in the reaction solutions with varied volume fractions of ethanol ( fR). The use of 9,10-bis(phenylethynyl) anthracene (BPEA) as a fluorescence probe unraveled a clear difference in interior structure between the CTAB micelles confined at different fR. At fR of 0.3, the confined CTAB micelles consisting of regularly and densely packed alkane chains, which created crystalline interiors, in which the doped BPEA molecules were effectively isolated in the monomeric form and well protected against aggressive attack from the surrounding environment. At fR of 0.4 or 0.5, the confined CTAB micelles consisting of less regularly but densely packed alkane chains created glassy interiors, which enabled reversible aggregation of the doped BPEA in response to the surrounding environmental change, for instance, the ethanol content in the particle dispersion. At fR of 0.6 or 0.7, the confined CTAB micelles consisting of loosely packed alkane chains created amorphous interiors, which offered sufficiently large free spaces to facilitate the material exchange with the surrounding environment, as evidenced by noticeable intake of the Pyronin Y molecules present in the particle dispersion. The revealed phase modulation of the interiors of surfactant micelles, confined in the pores of mesoporous particles, from crystalline to glassy and amorphous structures, which were scarcely reported in literature, will inspire rational design of mesoporous silica particles with desired technical performance according to the purposes of the practical application.

Growth of Mesoporous Silica Film with Vertical Channels on Substrate Using Gemini Surfactants

Synthesis of silica mesoporous crystals with controlled structure and morphology using gemini surfactant

Manufacture of Size Controllable Two-dimensional Mesoporous Silica via the Self-assembly of Gemini surfactants

Synthesis of Mesoporous Silica Spheres by Using Neutral-cationic Surfactant and Semi-batch Growth

Synthesis of mesoporous silica hollow spheres in supercritical CO2/water systems

Synthesis of monodispersed mesoporous silica spheres (MMSSs) with controlled particle size using gemini surfactant

The influences of the spacer of gemini surfactants on the structure of silicic mesoporous materials

Synthesis of siliceous hollow spheres with large mesopore wall structure by supercritical CO2-in-water interface templating.

Seeding-growth of Helical Mesoporous Silica Nanofibers Templated by Achiral Cationic Surfactant.

Emulsion droplets as a dynamic interface for the direct and large-scale synthesis of ultrathin free-standing mesoporous silica films as well as 2D polymeric and carbon nanomaterials.

Effects of Coating Methods on Microstructure and Optical Properties of Mesoporous Silica Films

Facile Synthesis Of Monodisperse Microspheres And Gigantic Hollow Shells Of Mesoporous Silica In Mixed Water-Ethanol Solvents

Synthesis of ordered small pore mesoporous silicates with tailorable pore structures and sizes by polyoxyethylene alkyl amine surfactant

Highly Ordered Mesoporous Silica Films with Perpendicular Mesochannels by a Simple Stöber‐Solution Growth Approach

Structural Control of Surfactant-Templated Hexagonal, Cubic, and Lamellar Mesoporous Silicate Thin Films Prepared by Spin-Casting

Synthesis of Continuous Mesoporous Silica Thin Films with Three-Dimensional Accessible Pore Structures

Preparation of Ordered 2-D Hexagonal Mesoporous Silica with Ultra Thick Pore Walls Using a Novel Nonionic Organosilicon Surfactant

Synthesis and Coating of Ordered Mesoporous Silica

Synthesis of Carboxylic Group Functionalized Monodispersed Mesoporous Silica Spheres (mmsss) Via Costructure Directing Method

Formation of Monodisperse Mesoporous Silica Microparticles Via Spray-Drying

Phase Engineering of Hydrophobic Meso-Environments in Silica Particles for Technical Performance Enrichment