Abstract:A series of HZSM-5 zeolites modified with various mass fractions of antimony oxide Sb2O3(0-30%) were prepared by solid state ion exchange method,and then physically mixed with an industrial methanol synthesis catalyst(XNC-98) to form a series of hybrid catalysts CuO-ZnO-Al2O3+Sb2O3/HZSM-5.The direct synthesis of dimethyl ether(DME) from syngas was carried out over the prepared hybrid catalysts under pressurized fixed-bed continuous flow conditions.The results indicated that over the CuO-ZnO-Al2O3+Sb2O3/HZSM-5 hybrid catalysts with suitable amount of Sb2O3 the selectivities of undesired byproducts hydrocarbons and CO2 were significantly decreased from 9.3% and 32.4% to less than 1% and 28%,respectively,and the selectivity for DME was enhanced greatly from 55% to 69% under temperature of 260℃,pressure of 4 MPa and gas hourly space velocity of 1500 ml/(g·h),compared with that over the unmodified HZSM-5 hybrid catalysts.It was clear from the results of NH3-TPD characterization that the decrease in the formation of hydrocarbons and CO2 could be attributed to the significant decline in the amount of strong acid sites induced by Sb2O3 modification.In addition,the influences of the operating parameters,including the reaction temperature,pressure and space velocity of feed on the catalytic performance of the hybrid catalysts were also investigated.It was shown that at high reaction temperature and high gas hourly space velocity both lower CO conversion and lower DME selectivity were obtained,the suitable reaction temperature and gas hourly space velocity would be less than 280℃ and 3000 ml/(g·h),respectively.

Effect of Modified Zeolite on One-Step Process of DME Synthesis

Effects of CaO-modified Zeolite on One-Step Synthesis of Dimethyl Ether

Acidity of Magnesium Oxide Modified HZSM-5 Zeolite and Its Application in the Direct Synthesis of Dimethyl Ether from Syngas--The Effect of Magnesium Precursor

Highly Efficient Synthesis of Dimethyl Ether from Syngas over the Admixed Catalyst of CuO–ZnO–Al2O3 and Antimony Oxide Modified HZSM-5 Zeolite

Preparation of Phosphorus-Modified Hzsm-5 Zeolite and Its Application in the One-Step Synthesis of Dimethyl Ether from Syngas

Effects of Ammonium Hexafluorosilicate Modification on Acidity of Hmcm-22 and Catalytic Performance of Cuo-Zno-Al2o3/Hmcm-22 for Dimethyl Ether Synthesis

Synthesis of Dimethyl Ether (DME) on Modified HY Zeolite and Modified HY Zeolite-Supported Cu–Mn–Zn Catalysts

Study on the Zeolite Catalysts for Dimethyl Ether Synthesis from Methanol

Enhancement of the dimethyl ether carbonylation activation via regulating acid sites distribution in FER zeolite framework

One-Step Synthesis of Dimethyl Ether from Syngas with Fe-Modified Zeolite ZSM-5 as Dehydration Catalyst

Comparison of Dimethyl Ether Carbonylation Performance over Some Zeolites Containing 8-Member Ring Pores

THE DIRECT SYNTHESIS OF DIMETHYL ETHER FROM SYNGAS OVER THE HYBRID CATALYST WITH ANTIMONY MODIFIED HZSM-5 ZEOLITE AS ACID COMPONENT

Dimethyl Ether Synthesis Via Methanol and Syngas over Rare Earth Metals Modified Zeolite Y and Dual Cu–Mn–Zn Catalysts

Effects of MgO modification to HZSM-5 Zeolite for LPG synthesis

Influence of SiO2/Al2O3 ratio in HMCM-22 on catalytic performance of Cu2ZnO2Al2O3/HMCM-22 for synthesis of dimethyl ether

Preparation, Structure And Performance Of [Cuo-Zno-Al2o3]/[Hzsm-5] Core-Shell Bifunctional Catalysts For One-Step Synthesis Of Dimethyl Ether From Co2+H-2

Modification of acidity in HZSM-5 zeolite for methane-methanol co-reaction

An Effective Catalyst for Syngas-To-Dimethyl Ether Process with Steamed Zeolite Hmcm-49 As Dehydration Component

Synthesis of Hierarchical Porous H-mordenite Zeolite for Carbonylation of Dimethyl Ether

Characterization of Cu-Mn/Zeolite-Y Catalyst for One-Step Synthesis of Dimethyl Ether from Co-H-2

Dimethyl Ether Synthesis from CO2 Hydrogenation on a CuO−ZnO−Al2O3−ZrO2/HZSM-5 Bifunctional Catalyst