Abstract:A large amount of directional and willow-like β′ phase was precipitated in Mg–10Gd–3Y–0.4Zr (GW103K) alloy after solution treatment and subsequently aged treatment (T6). In order to explore the effect of the precipitates on the corrosion behavior of the GW103K alloy, the alloy was subjected to solution treatment (T4) at 773 K for 4 h at first, subsequently aged at 498 K for 193 h (T6). The microstructure evolution of the GW103K alloy after this treatment was investigated by scanning electron microscopy and transmission electron microscopy. The high-angle annular detector dark-field scanning transmission electron microscopy was used to observe the typical corrosion morphologies of the nanoscale precipitation phases (β′) in the T6-treated alloy. The corrosion rate was measured by potentiodynamic polarization test. Combining with the potential measurement results by scanning Kelvin probe force microscopy, the effects of the skeleton-like Mg24(Gd, Y)5 and β′ precipitates on the corrosion behavior of GW103K alloy were explored. The results showed that the corrosion rate of the GW103K alloy in different conditions was ranked as: as-cast alloy> T4-treated alloy> T6-treated alloy, attributing to the fact that the relative potential differences of skeleton-like Mg24(Gd, Y)5 were lower than those of the matrix, therefore Mg24(Gd, Y)5 phase formed micro-galvanic coupling with the matrix and corrosion dissolution occurred. The nanoscale β′ precipitates in T6-treated alloy can retard the cathodic process.

Inhibition Effect of Inorganic and Organic Inhibitors on the Corrosion of Mg–10Gd–3Y–0.5Zr Alloy in an Ethylene Glycol Solution at Ambient and Elevated Temperatures

Self-corrosion, galvanic corrosion and inhibition of GW103 and AZ91D Mg alloys in ethylene glycol solution

The synergistic inhibition effect of organic silicate and inorganic Zn salt on corrosion of Mg-10Gd-3Y magnesium alloy

Galvanic Corrosion and Inhibition of GW103 and AZ91D Mg alloys coupled to an al alloy in an ethylene glycol solution at ambient and elevated temperatures

Effect of Different Scale Precipitates on Corrosion Behavior of Mg–10Gd–3Y–0.4Zr Alloy

Investigation of the Corrosion for Mg–xGd–3Y–0.4Zr (x = 6, 8, 10, 12 Wt%) Alloys in a Peak-Aged Condition

Inhibition Mechanism of Interaction Effect Between Charged Character of Inhibitor and Rare Earth Elements for Mg-Gd-Y Alloy

Investigation of Corrosion Behaviors of Mg–6Gd–3Y–0.4Zr Alloy in NaCl Aqueous Solutions

Improving Environmental Adaptability and Long-Term Corrosion Resistance of Mg Alloys by Pyrazole Ionic Liquids: Experimental and Theoretical Studies

Corrosion Inhibition of Aluminum Alloy in 50% Ethylene Glycol Solution

Comparative Study on Corrosion Behavior and Mechanism of As-Cast Mg–Zn–Y and Mg–Zn–Gd Alloys

Influence of Interactions Between Β′ Precipitates and Long Period Stacking Ordered Structures on Corrosion Behaviors of Mg–10Gd–5Y–2Zn–0.5Zr (wt%) Alloy

Study of corrosion inhibitors on AZ91D magnesium alloy

Biodegradable behaviors in simulated body fluid of Mg-Gd-Y-Zr alloy with micro-arc oxide coating

New Understanding on the Mechanism of Organic Inhibitors for Magnesium Alloy

Effect of Gd on Microstructure and Corrosion Resistance of As-Cast Mg97Zn1Y2 Alloy

A Study on Corrosion Inhibitor for Magnesium Alloy

Improving the corrosion resistance of MgZn1.2Gd Zr0.18 (x = 0, 0.8, 1.4, 2.0) alloys via Gd additions

Corrosion Performance and Mechanical Properties of Sputter-Deposited MgY and MgGd Alloys

Corrosion Behavior and Mechanism of Mg-Y-Zn-Zr Alloys with Various Y/Zn Mole Ratios

Corrosion behavior of Mg-10Gd-2Y-0.4Zr alloy under thin electrolyte layers