Degradation of Poly(L-lactide) Films under Ultraviolet Irradiation and Water Bath

Chunmei Zhang,Changzhen Man,Weiwei Wang,Long Jiang,Yi Dan
DOI: https://doi.org/10.1080/03602559.2011.551970
2011-01-01
Polymer-Plastics Technology and Engineering
Abstract:Poly(L-lactide) (PLLA) films were exposed to ultraviolet (UV) light (254nm) and water bath of 60 degrees C and 80 degrees C. The limiting viscosity ([]) of PLLA decreased from initial 187.4 dl/g to 42.2 dl/g after UV irradiation, and to 33.3 dl/g after soaking in 80 degrees C water for 40h, while the [] of PLLA exposed to 60 degrees C water remained at 115.6 dl/g after 40h. Compared with the original PLLA, the degraded PLLA was bimodal in the GPC profile. FTIR analysis showed that the chain scission of PLLA acted by water molecules resulted in a C=C structure.