Abstract:In this article, we report a controllable and reproducible approach to prepare highly ordered 2-D hexagonal mesoporous crystalline TiO2-SiO2 nanocomposites with variable Ti/Si ratios (0 to infinity). XRD, TEM, and N2 sorption techniques have been used to systematically investigate the pore wall structure, and thermal stability functioned with the synthetic conditions. The resultant materials are ultra highly stable (over 900 degrees C), have large uniform pore diameters (approximately 6.8 nm), and have high Brunauer-Emmett-Teller specific surface areas (approximately 290 m2/g). These mesostructured TiO2-SiO2 composites were obtained using titanium isopropoxide (TIPO) and tetraethyl orthosilicate (TEOS) as precursors and triblock copolymer P123 as a template based on the solvent evaporation-induced co-self-assembly process under a large amount of HCl. Our strategy was the synchronous assembly of titanate and silicate oligomers with triblock copolymer P123 by finely tuning the relative humidity of the surrounding atmosphere and evaporation temperature according to the Ti/Si ratio. We added a large amount of acidity to lower condensation and polymerization rates of TIPO and accelerate the rates for TEOS molecules. TEM and XRD measurements clearly show that the titania is made of highly crystalline anatase nanoparticles, which are uniformly embedded in the pore walls to form the "bricked-mortar" frameworks. The amorphous silica acts as a glue linking the TiO2 nanocrystals and improves the thermal stability. As the silica contents increase, the thermal stability of the resulting mesoporous TiO2-SiO2 nanocomposites increases and the size of anatase nanocrystals decreases. Our results show that the unique composite frameworks make the mesostructures overwhelmingly stable; even with high Ti/Si ratios (> or =80/20) the stability of the composites is higher than 900 degrees C. The mesoporous TiO2-SiO2 nanocomposites exhibit excellent photocatalytic activities (which are higher than that for commercial catalyst P25) for the degradation of rhodamine B in aqueous suspension. The excellent photocatalytic activities are ascribed to the bifunctional effect of highly crystallized anatase nanoparticles and high porosity.

Templated Synthesis of Shape-Controlled, Ordered Tio2 Cage Structures

Synthesis and Layer-by-layer Self-Assembly of Titania Nanosheets Controllably Doped with Binary Transition Metal Ions

Controllable Synthesis of Tio2 Single Crystals with Tunable Shapes Using Ammonium-Exchanged Titanate Nanowires As Precursors

A facile synthesis of hierarchical TiO<sub>2</sub>for dye adsorption and photocatalysis

Controlled synthesis of ordered mesoporous C-TiO2 nanocomposites with crystalline titania frameworks from organic-inorganic-amphiphilic coassembly

Self-assembly and Photocatalysis of Mesoporous TiO 2 Nanocrystal Clusters

A facile synthesis of hierarchical TiO2 for dye adsorption and photocatalysis

Template-free Synthesis of Titania Architectures with Controlled Morphology Evolution

One Step Route to the Fabrication of Arrays of Tio2 Nanobowls Via A Complementary Block Copolymer Templating and Sol-Gel Process

Facile and large-scale synthesis of hollow TiO2 nanostructures from TiCl3 solution

Space-Confined seeding and growth of ordered arrays of TiO2 hierarchical nanostructures

Live Templates of a Supramolecular Block Copolymer for the Synthesis of Ordered Nanostructured TiO2 Films via Guest Exchange

Shape‐ and Size‐Controlled Synthesis of Uniform Anatase TiO2 Nanocuboids Enclosed by Active {100} and {001} Facets

Synthesis of Mesoporous TiO2 with a Crystalline Framework

Ligand‐Assisted Assembly Approach to Synthesize Large‐Pore Ordered Mesoporous Titania with Thermally Stable and Crystalline Framework

From Titanates to TiO 2 Nanostructures:Controllable Synthesis,growth Mechanism,and Applications

Controllable synthesis and self-template phase transition of hydrous TiO2 colloidal spheres for photo/electrochemical applications

Synthesis of Tio 2 Meso-Structured Thin Films

Template-based Synthesis and Micro-structure Characterization of TiO2 Nano-array

Controllable and Repeatable Synthesis of Thermally Stable Anatase Nanocrystal-Silica Composites with Highly Ordered Hexagonal Mesostructures.

Controlled Synthesis of Titanium Dioxide Nanostructures