Abstract:In this paper, the hemicelluloses (HCB) isolated from corncobs were modified by click chemistry. The introduction of azide functionalities into the backbone of the polysaccharide was done in DMF/LiCl at 100 degrees C for 24h in presence of sodium azide and the pre-modified hemicellulose with 2-bromoisobutyl bromide (BiBB) through esterification reaction which was processed under ambient temperature for 24 h. The chemical structure of the products obtained in each step was precisely characterized by FTIR as well as NMR. Moreover, the achieved degree of substitution of azide groups in the hemicelluloses which was characterized by elemental analysis was up to 0.23. Alkyne-terminated functionalized NIPAAm-co-HEMA (ANCH) copolymer was then grafted onto the synthesized azide-functionalized hemicelluloses (HBN) with different DS of the azide groups varying from 0.08 to 0.23 by copper-catalyzed azide-alkyne cycloaddition (CuAAC), a typical reaction of click chemistry, at 80 degrees C for 8h to form the novel temperature sensitive hemicellulose-based hydrogels (HNG).Their temperature sensitivity and morphology were investigated by DSC and SEM. From the results, it can be seen that the LCST of the hydrogels were increased with the increase of the DS of the azide groups in BEN, whereas, the pore size of the hydrogels was decreased with increasing the azide groups' DS. Comparing with those reported photo-crosslinking and free radical copolymerization methods, click chemistry could not only shorten the formation time of such hydrogels, but also endow them with more uniform pore structure due to its features of high stereospecificity, selectivity and high efficiency. Besides, the drug loading and releasing behavior of the hydrogels were discussed as well.

Thermal Sensitive Hydrogels Prepared From Hemicelluloses Ultrasonically Extracted From Corncob

Production of Xylooligosaccharides from Corncobs by Xylanase Hydrolysis

Properties of Hemicellulose-Based Hydrogels Synthesized via ATRP

Synthesis and characterization of temperature sensitive hemicellulose-based hydrogels

Preparation of a high-performance conductive lignocellulose hydrogel by directly using non-detoxified bisulfite-pretreated corncob

Preparation Of The Temperature Sensitive Hemicellulose-Based Hydrogels Via Click Chemistry

Isolation And Characterization Of Corncob Cellulose Fibers Using Microwave-Assisted Chemical Treatments

Effect of Ultrasonic Time on the Structural and Physico-Chemical Properties of Hemicelluloses from Eucalyptus Grandis.

Isolation and Characterization of Corn Stover Hemicellulose

Structural characteristics of corncob and eucalyptus contributed to sugar release during hydrothermal pretreatment and enzymatic hydrolysis

Preparation and Swelling Behaviors of Porous Hemicellulose‐g‐polyacrylamide Hydrogels

Preparation and Characterization of Temperature- and Ph-Sensitive Hemicellulose-Containing Hydrogels

Xylan Sulphates Prepared Via Microwave-Assisted Esterifications Reaction From Corncob

Xylo-sugars Production by Microwave-Induced Hydrothermal Treatment of Corncob: Trace Sodium Hydroxide Addition for Suppression of Side Effects

Synthesis and Properties of Hemicelluloses-Based Semi-Ipn Hydrogels.

Modification of the Water-Insoluble Hemicelluloses Via Free Radical Copolymerization in Diluted Alkali Aqueous Medium

Production of Xylo-Sugars from Corncob by Oxalic Acid-Assisted Ball Milling and Microwave-Induced Hydrothermal Treatments

Synthesis And Properties Of Temperature-Sensitive Hydrogel Based On Hydroxyethyl Cellulose

Cellulose fibers extracted from rice and oat husks and their application in hydrogel

Synthesis And Characterization Of Super-Absorbent Hydrogels Based On Hemicellulose

A Simple Method for the Production of Hydrogels Based on Hemicellulose in Aqueous Solution