Size Control of Zno Nano-Particles Formed Via Thermal-Decomposition Route

L. Z. Zhang,M. G. Yi,L. Xiang,B. Y. Wang

DOI: https://doi.org/10.1063/1.3529311

2010-01-01

Abstract:ZnO nano‐particles with a particle size of 30–60 nm were fabricated by thermal decomposition of the basic zinc carbonate (2ZnCO3⋅3Zn(OH)2⋅H2O) precursor at 400–600° C for 1.0–2.0 h, using ZnSO4 and Na2CO3 as the reactants. The particle size of ZnO was connected with the sintering temperature and procedure. The increase of temperature from 300° C to 600° C led to the increase of the crystallinity and the particle size of ZnO. Compared with the one‐step sintering, the multi‐step sintering favored the formation of dispersive ZnO nano‐particles with smaller sizes. The presence of minor amount of sodium dodecyl sulfate (SDS, C12H25NaO4S) inhibited the growth and the agglomeration of the ZnO particles, reducing the primary particle size from 60–100 nm to 30–60 nm.