Abstract:High-silicon and molybdenum (SiMo) ductile iron is a common heat-resistant alloy that may be exposed to high-temperature wear during service in many of its applications. The wear behavior of four SiMo ductile iron alloys was evaluated at different temperatures up to 750 °C. This research focuses on the influence of various Mo contents on the microstructure, structural stability, and hence, the wear performance of such alloys. Thermodynamic calculations proposed the phase diagrams, critical transformation temperatures, and phase volume fractions in all samples by means of Thermo-Calc software. The dilatometry measurements were carried for confirming the theoretical results of Thermo-Calc thermodynamic calculations. The results revealed that the microstructure of SiMo ductile cast iron consists of nodular graphite and a ferrite matrix with carbides embedded in the fine precipitates at the grain boundary regions. The type of carbides and the nature of these fine precipitates are discussed according to EDX and SEM results. Adding molybdenum enhanced the wear performance of SiMo by decreasing the weight loss by about 40–70% compared to a Mo-free alloy. This is due to the increased molybdenum carbides, which increase hardness and improve wear resistance in SiMo alloys. The high temperatures have a negative effect on reducing the wear resistance at 250 °C. On the other hand, the wear resistance unexpectedly started to increase at higher temperatures of 500 °C and 750 °C because of the contribution of oxidative wear with abrasive wear by forming a protective oxide layer. Furthermore, the obtained results supported the idea that adding molybdenum improves wear resistance at high temperatures. Hence, SiMo has the potential to be wear-resistant material in wider applications requiring high-temperature wear resistance.

Friction Properties of Molybdenum Alloyed Steel at Elevated Temperatures

The Thermal Stability and Lubricity of Zinc Thiomolybdenate at Temperatures Up to 500°C

The Synergistic Effects Of Mo As An Alloy Element Added To Chromium Carbide Coatings On Their Lubrication Properties At High-Temperatures

Investigation of the elevated temperature tribological property and wear mechanism of Fe‐15Cu‐0.8C materials containing Mo‐coated MoS2 powders

Tribological properties of molybdenum ion-plated and ion-sulfurized composite coating on mild steel

High-Temperature Friction and Wear Behavior of Nickel-Alloy Matrix Composites with the Addition of Molybdate

Tribological Properties of Antifriction Molybdenum Disulfide Coatings under Extreme Conditions

Effect of Molybdenum Contents on Microstructure and High-Temperature Wear Behavior of SiMo Ductile Iron

The effect of temperature on the unlubricated sliding wear of 5 CrNiMo steel against 40 MnB steel in the range 400–600°C

Novel Anti-Wear Performance of Nano Magnesium Silicate Hydroxide in Boundary Lubrication Under High Temperature

Effect of molybdenum on the oxidation resistance of FeCrAl alloy in lower temperature (400 °C) and higher temperature (1200 °C) steam environments

Aplysia Californica as a Novel Source of Material for Biohybrid Robots and Organic Machines

Friction and wear performance of laser clad Mo modified Stellite 12 matrix coatings at elevated temperature

Effect of MoS 2 element diffusion under high temperature condition on the tribological properties of cemented carbide materials

High temperature induced “glaze” layer formed in HVOF-sprayed NiCrWMoCuCBFe coating and its wear reduction mechanism

High temperature tribological behavior of Mo–12Si–8.5B alloy reinforced with MoAlB ceramic

Performance Study of MCrAlY Flame Sprayed Coating on AISI 304 Stainless Steel of Microstructure and Sliding Wear at High Temperatures

Tribo-induced surface structure of Nickel-based superalloy at elevated temperature

High temperature tribological behaviors and wear mechanisms of NiAl-MoO3/CuO composite coatings

Magnesium Silicate Hydroxide–MoS2–Sb2O3 Coating Nanomaterials for High-Temperature Superlubricity

The Influence of Alkali Metal Polyphosphate on the Tribological Properties of Heavily Loaded Steel on Steel Contacts at Elevated Temperatures