Abstract:Organic field-effect transistors (OFETs) have acquired increasing attention because of their wide range of potential applications in electronics; nevertheless, high operating voltage and low carrier mobility are considered as major bottlenecks in their commercialization. In this work, we demonstrate low-voltage, flexible OFETs based on ultrathin single-crystal microribbons. Flexible OFETs fabricated with 2,7-dioctylbenzothieno[3,2-b]benzothiophene (C8-BTBT) based solution-processed ultrathin single-crystal microribbon as the semiconductor layer and high-k polymer, polysiloxane-poly(vinyl alcohol) composite as an insulator layer manifest a significantly low operating voltage of -4 V, and several devices showed a high mobility of >30 cm2 V-1 s-1. Besides, the carrier mobility of the fabricated devices exhibits a slight degradation in static bending condition, which can be retained by 83.3% compared with its original value under a bending radius of 9 mm. As compared to the bulk C8-BTBT single-crystal-based OFET, which showed a large crack only after 50 dynamic bending cycles, our ultrathin single-crystal-based counterpart demonstrates a much better dynamic force stability. Moreover, under a 20 mm bending radius, the mobility of the device decreased by only 11.7% even after 500 bending cycles and no further decrease was observed until 1000 bending cycles. Our findings reveal that ultrathin C8-BTBT single-crystal-based flexible OFETs are promising candidates for various high-performance flexible electronic devices.

Electrical Response of Flexible Vanadyl-Phthalocyanine Thin-Film Transistors under Bending Conditions

Electrical Instability In Vanadyl-Phthalocyanine Thin-Film Transistors

High Performance Vanadyl Phthalocyanine Thin-Film Transistors Based on Fluorobenzene End-Capped Quaterthiophene As the Inducing Layer

The mechanical bending effect and mechanism of high performance and low-voltage flexible organic thin-film transistors with a cross-linked PVP dielectric layer

High Mobility Vanadyl-Phthalocyanine Polycrystalline Films For Organic Field-Effect Transistors

Electrical Properties in Vanadyl-Phthalocyanine-based Metal-Insulator-semiconductor Devices

High elasticity of CsPbBr 3 perovskite nanowires for flexible electronics

Flexible Low-Voltage IGZO Thin-Film Transistors with Polymer Electret Gate Dielectrics on Paper Substrates

Flexible VO2 thermochromic films with narrow hysteresis loops

High-Performance Flexible ZnO Thin-Film Transistors by Atomic Layer Deposition

Phthalocyanine derivatives for solution-processed organic thin-film transistors

High reliability of vanadyl-phthalocyanine thin-film transistors using silicon nitride gate insulator

Inkjet Printing PVP Dielectric for Flexible Thin Film Transistor

Highly Flexible Electronics from Scalable Vertical Thin Film Transistors

Mixed‐Dimensional Van Der Waals Engineering for Charge Transfer Enables Wafer‐Level Flexible Electronics

Flexible High-Entropy Poly(vinyl Alcohol) Dielectric Films Were Prepared at a Low Temperature and Applied to an Indium Gallium Zinc Oxide Thin-Film Transistor.

36.3: Flexible ZnO Thin‐Film Transistors Fabricated on PEN Substrate by Atomic Layer Deposition at Low Temperature

Modulating the Transport Property of Flexible La0.67Ca0.33MnO3 Thin Film by Mechanical Bending

Flexible field-effect transistors with a high on/off current ratio based on large-area single-crystal graphene

Low-voltage operating, high mobility top-gate structural flexible organic thin-film transistor with a one-step spin-coated binary polymer gate dielectric

Low-Voltage, High Performance Flexible Organic Field Effect Transistors Based on Ultrathin Single Crystal Microribbons.