Abstract:With pure Ti and pure Zr as controls, the corrosion resistance, ion release behavior, and in vitro biocompatibility of Be-containing Zr41Ti14Cu12Ni10Be23 bulk metallic glass (BMG) (LM1), Zr44Ti11Cu10Ni10Be25 BMG (LM1b), and Be-free Zr57Nb5Cu15.4Ni12.6Al10 BMG (LM106) were investigated in terms of electrochemical measurements in simulated body fluid (SBF) with pH value 7.4 and artificial saliva (AS) with pH value 6.3, and 3-[4,4-dimethylthiazol-2-yl]-2,5-diphenyltetrazolium bromide (MTT) assay using L929 and NIH3T3 cells, aiming to assess the feasibility of Zr-based BMGs as potential biomaterial. It was found that LM1b showed superior corrosion resistance to LM106 and LM1 in both SBF and AS, and comparable with pure Ti and pure Zr. After 7200 s immersion, a two-layer structure oxide film was formed on LM1, LM1b, and pure Zr surfaces, while one-layer structure oxide film was formed on LM106 and pure Ti surfaces. The pitting corrosion potentials of LM1b were much higher than that of LM1, LM106, and pure Zr, resulting in very few ions releasing into the electrolytes. No Be ion could be detected but a little amount of Cu ion was detected for LM106, LM1, and LM1b after immersion in Dulbecco's modified Eagle's medium for 72 h at 37 degrees C. The indirect cytotoxicity results show that LM106, LM1, and LM1b extracts had no cytotoxicity to L929 and NIH3T3 cells. The direct cytotoxicity results show that cells could adhere well on the Zr-based BMG surface as in pure Ti and Zr. Lower cell proliferation rate of LM106 and LM1 is observed when compared with LM1b, which was found to be caused by Cu ion releasing rather than by Be ion. (C) 2010 Wiley Periodicals, Inc. J Biomed Mater Res Part B: Appl Biomater 96B: 34-46,2011.

Correlation Between Corrosion Performance And Surface Wettability In Zrticunibe Bulk Metallic Glasses

An Abnormal Correlation Between Electron Work Function and Corrosion Resistance in Ti-Zr-Be-(Ni/Fe) Metallic Glasses

Effect of Copper Content on Glass -Forming Ability and Corrosion Resistance of Novel A1NiZrCoYSi High Entropy Amorphous Alloy

The Pitting Corrosion Behavior of Shear Bands in A Zr-Based Bulk Metallic Glass

In Vitro Study On Zr-Based Bulk Metallic Glasses As Potential Biomaterials

Corrosion mechanisms of Zr-based bulk metallic glasses in NaBr solution

Corrosion Behavior of TiZrHfBeCu(Ni) High-Entropy Bulk Metallic Glasses in 3.5 Wt. % NaCl

Effect of Nb Substitution for Cu on Glass Formation and Corrosion Behavior of Zr Cu Ag Al Be Bulk Metallic Glass

Effects of nanoscale chemical heterogeneity on the wear, corrosion, and tribocorrosion resistance of Zr-based thin film metallic glasses

A Novel Ni-Free Zr-Based Bulk Metallic Glass with High Glass Forming Ability, Corrosion Resistance and Thermal Stability

Wetting Behavior of LBE on Corroded Candidate LFR Structural Materials of 316L, T91 and CLAM

Study on corrosion and wear behavior mechanism of Zr-based bulk amorphous

Effects of Cu Addition on the Glass Forming Ability and Corrosion Resistance of Ti-Zr-Be-Ni Alloys

Facile Electrochemical Method for the Fabrication of Stable Corrosion-Resistant Superhydrophobic Surfaces on Zr-Based Bulk Metallic Glasses

Thermal Oxidation Effect on Corrosion Behavior of Zr46Cu37.6Ag8.4Al8 Bulk Metallic Glass

Electrochemical surface nanostructuring of Ti47Cu38Fe2.5Zr7.5Sn2Si1Ag2 metallic glass for improved pitting corrosion resistance

Effect of Thermal Oxidization on Corrosion Behavior of Zr-based Bulk Metallic Glass

Corrosion Of, and Cellular Responses to Mg–Zn–Ca Bulk Metallic Glasses

Corrosion behavior of ZrN coated ferritic/martensitic steel in liquid lead-bismuth eutectic

Enhanced pitting corrosion resistance of a Zr-based metallic glass by ultraviolet light irradiation

Fast Screening of Corrosion Trends in Metallic Glasses