Abstract:The influence of the final-annealing parameters and pretreatment before etching on the etching ability of the high voltage aluminum foils was investigated. The distribution of pits and the morphological features after etching were observed by metallographic microscopy and scanning electron microscopy. The galvano-chemistry performance of foils was analyzed by using polarization curve. The results show that when the foils are annealed at various temperatures (470-560°C) for different annealing times (0.5-4 h), the best annealing technology is at 500°C for 1 h, which will increase the concentration as well as the distribution homogeneity of the trace elements in the surface layer; it will get bad result if the annealing temperature or the time is increased. The sodium hydroxide pretreatment before pitting can remove the oxide film of the foils, and the hydrochloric acid pretreatment makes Cl- ion enter into the surface of foils. NaOH+HCl pretreatment reduces the corrosion potential and promotes the pitting of the aluminum foils; the area and density of pit etching on the aluminum surface increase after pretreatment, and the uniformity of pitting also increases significantly.

Influence of final-annealing and pretreatment before etching on pitting ability of aluminum foils