Mechanical properties and microstructural analysis of AXJ530 magnesiu alloy reinforced with alumina fibers

Bin Hu,L. M. Peng,Bob R. Powell,Anil K. Sachdev

2010-01-01

Abstract:AXJ530-based magnesium matrix composites containing 15 volume percent, silica-bonded Saffil RF Al2O3 fiber reinforcement were fabricated and characterized. Disk-shaped reinforcement preforms were infiltrated with the molten alloy (Mg-5A1-3Ca-0.15Sr, units as wt percent) by direct squeeze casting. Infiltration conditions were optimized to yield pore-free composites exhibiting homogenous distribution of Al2O3 fibers in the magnesium matrix. A steel housing around the preform was shown to be necessary to avoid preform distortion and fracture during infiltration. The microstructure, tensile properties, creep behavior, and interface chemistry of the composites were investigated. The composites showed 30% higher ultimate tensile strength and 90% greater yield strength compared with the unreinforced AXJ530 alloy. However, there was a marked decrease (60%) in ductility. Nevertheless, inspection of the fracture surfaces showed pullout of the fibers was more common than fiber fracture. The creep resistance of the composite was improved relative to the unreinforced alloy; the secondary creep rates being 1.38x10(-9)s(-1) vs. 4.73x10(-9)s(-1), respectively. It was found that the matrix/fiber interface was enriched with Si (from the binder agent) and Ca, an alloying element in AXJ530. DTA showed the melt temperature of the composite was only 4 degrees C higher that of the matrix alloy which indicated the interfacial reaction of melt with fiber and binder is weak.