Abstract:Calcium silicate (CS) is a main component of Portland cement and is responsible for the strength development. Recent research has shown that dicalcium silicate cement (CSC) is bioactive and is a potential candidate for bone replacement. Traditionally, dicalcium silicate powder is synthesized by a solid state reaction or a sol-gel method. The solid-state reaction, however, usually needs a higher temperature and a longer calcination time. Furthermore, the dicalcium silicate powder made by the sol-gel method is not pure, and contains a significant quantity of CaO which is harmful to the strength and biological properties of the CSC. The Pechini technique is an alternative, low temperature polymeric precursor route for synthesis of high purity powders. In this study, purer CS powder was synthesized via the Pechini method by calcination at 800°C for 3h. DSC-TGA, XRD, SEM were used for characterization of CS powder and the hydrated cement. The DSC-TGA curves showed that the main exothermic peak was at 479°C and the total mass loss was 79.2%. The XRD patterns of CSC after hydration for 7, 14, and 35 days illustrated that dicalcium silicate hydrate (Ca1.5SiO3.5·xH2O, C-S-H) was formed in the hardened CS paste. The XRD peaks on the diffraction pattern of the C-S-H of the day 35 sample were of greater intensity than those at day 7 and day 14. This demonstrates that the hydration speed was slow and complete hydration could take more than one month. Flake-like crystals were observed on scanning electron micrographs following hardening. The degradation study result showed that there was no mass loss of CSC after the samples were soaked into phosphate buffered saline (PBS) for 40 days. The silicon assay revealed that orthosilicic acid could be released from CSC after the samples were soaked in simulated body fluid (SBF). Silicon is known to be critical to skeletal mineralization. The existence of silicon may stimulate the proliferation of bone and activate cells to produce bone. Investigation of cell attachment confirmed that the MC-3T3 cells attached well to the surfaces of CSC after seeding.

Comparing Three Methods for the Synthesis of Pure Beta-Dicalcium Silicate

Synthesis of Pure Tricalcium Silicate Powder by the Pechini Method and Characterization of Hydrated Cement

Systematic Investigation of Β-Dicalcium Silicate-Based Bone Cements in Vitro and in Vivo in Comparison with Clinically Applied Calcium Phosphate Cement and Bio-Oss®

Green Synthesis of Calcium Silicate Bioceramic Powders

Composition control in biphasic silicate microspheres on stimulating new bone regeneration and repair of osteoporotic femoral bone defect

Calcium silicate cements prepared by hydrothermal synthesis for bone repair

Green Synthesis and Bioactivity of Vaterite-Doped Beta-Dicalcium Silicate Bone Cement

Initial Hydration Process of Calcium Silicates in Portland Cement: A Comprehensive Comparison from Molecular Dynamics Simulations

Synthesis of alite, belite and ferrite in both monophase and polyphase states and their hydration behavior

A novel and facile synthesis of calcium silicate nanoparticles as a base for root canal cement/sealer under constant potential: Compared to chemical synthesis

Optimization of Process Parameters for Synthesizing Cement Mineral Based on Nano-Technique

Optimal Design and Preparation of Beta-Sialon Multiphase Materials from Natural Clay

Preparation and in vitro bioactivities of calcium silicate nanophase materials

In Vitro Self‐setting Properties, Bioactivity, and Antibacterial Ability of a Silicate‐based Premixed Bone Cement

Novel Synthesis Method of Ca3al2o6 Using an Ethanol Solution Technique

Hydration activity, crystal structural, and electronic properties studies of Ba-doped dicalcium silicate

Comparison of the Properties of Calcium Silicates Derived from Different Raw Materials

Preparation of Tricalcium Silicate and Investigation of Hydrated Cement

A Simple Sol-Gel Technique for Synthesis of Nanostructured Hydroxyapatite, Tricalcium Phosphate and Biphasic Powders

Preparation and Characterization of Iron-Doped Tricalcium Silicate-Based Bone Cement as a Bone Repair Material

Composition design and microstructural characterization of calcined kaolin-based geopolymer cement