Abstract:The synthesis of SnO 2 nanoparticles doped with varying concentrations of Fe was carried out using the sol–gel method. The resulting samples underwent analysis using X-ray diffraction (XRD), high-resolution transmission electron microscopy (HR-TEM), ultraviolet–visible spectroscopy (UV–Vis), diffuse reflectance spectroscopy (DRS), photoluminescence spectroscopy, and vibrating sample magnetometry. The purpose of this investigation was to examine the impact of doping on the structural, optical, and magnetic properties of the nanoparticles. The XRD study demonstrated a discernible alteration in the size of the crystalline structure as a function of the concentration of doping. The study revealed a noticeable variation in crystallite size, ranging from ~ 13 to 5 nm, as the Fe doping concentration increased from 0 to 7 mol%. This observation suggested that the rise in Fe content effectively hindered crystal development. The estimation of the optical band gap was performed using the Kubelka–Munk equation, revealing a decrease in the band gap for a specific doping concentration of Fe. The photoluminescence (PL) spectra obtained at room temperature indicated a red shift in the peak positions of the pristine SnO 2 samples upon Fe doping. This observation provides confirmation of the reduction in the band gap of SnO 2 resulting from the incorporation of Fe dopants. The nanoparticles doped with 5% Fe exhibited superior optical characteristics compared to the remaining samples. Furthermore, magnetic properties were determined by investigating magnetization vs. applied fields. Ferromagnetic interaction was observed in all the systems of SnO 2 doped with Fe. To achieve a comprehensive understanding, the utilization of density functional theory was employed. The electronic states and density of states behavior were computed to accurately anticipate the arrangement of lattice sites and the corresponding presence of atoms. Theoretical computations were conducted using the VASP program.

Microstructure and magnetic properties in Sn1-xFexO2 (x = 0.01, 0.05, 0.10) nanoparticles synthesized by hydrothermal method

Synthesis of Nanocrystalline Ferrites Zn0.4ni0.6cr0.5laxfe1.5-Xo4 and Its Magnetic Properties

Effects of Fe Doping on Defects, Structural Disorder, and Optical and Magnetic Properties of SnO2 Nanoparticles

Structure and magnetic properties of SnFe2O4 nanoparticles

Structure and Magnetic Properties in Mn Doped SnO2 Nanoparticles Synthesized by Chemical Co-Precipitation Method

Room temperature Ferromagnetism in Th1-xFexO2-d (x = 0.0, 0.05, 0.10, 0.15, 0.20 and 0.25) nanoparticles

Synthesis and Magnetic Properties of SnFe2O4 Nanoparticles

Preparation and Magnetic Properties of Fe3+–Nb5+ Co-Doped SnO2

Microstructure And Optical Properties Of Fe-Doped Sno2 Nanoparticles Synthesized By Hydrothermal Method

Synthesis of Fe3+-modified SnO2 nanoparticles by hydrothermal method

Magnetic properties and local structure studies of Zn doped ferrites

Microstructure and Magnetic Properties of Cobalt-Doped SnO2 Nano-Powders

The Ferromagnetism of Sn1−xFexO2 Films and Nanostructure Arrays Prepared by Magnetron Sputtering

Mössbauer and magnetic studies of Fe-doped ZnO nanoparticles prepared by solution co-precipitation method

Synthesis and characterization of Fe3-xSnxO4 (X = 0–0.5) soft magnetic materials by low-temperature solid state method

Synthesis and characteristics of Fe3+-doped SnO2 nanoparticles via sol–gel-calcination or sol–gel-hydrothermal route

Effects of Hydroxyls on the Structural and Room Temperature Ferromagnetic Properties of Co Doped SnO2 Nanoparticles

Microstructure and magnetic properties of multiferroic CuCr1-xSnxO2 (x = 0–0.05) ceramics

Structural and Magnetic Properties of Chemically Synthesized Sn1−xMnxO2 Nanocrystalline Powders

Synergistic Insights into the Structural, Optical, and Magnetic Features of Iron-Modified Tin Oxide (Fe-SnO2) Nanoparticles: An Integrated Experimental and First Principles Investigation

Spin-Glass Transitions in Zn1-xFexO Nanoparticles