Effect of LiSbO3 Content on the Microstructure and Piezoelectric Properties of K0.5Na0.5NbO3 Lead-free Ceramics Doped with BiMnO3
Jiang Min-Hong,Liu Xin-Yu,Chen Guo-Hua,Zhu Gui-Sheng,Xu Ji-Wen,Ma Jia-Feng
DOI: https://doi.org/10.3724/sp.j.1077.2013.12229
IF: 1.292
2013-01-01
Journal of Inorganic Materials
Abstract:Lead-free (0.996-x)KNN-0.004BM-xLS (x=0, 0.01, 0.02, 0.03, 0.04, 0.05, 0.06) ceramics were prepared by the traditional ceramic sintering processing. The effect of LS content on the microstructure and piezoelectric properties of KNN-BM lead-free ceramics was investigated. The results show that the ceramics have a single orthorhombic phase structure when x <= 0.02, a co-existed phases orthorhombic and tetragonal phases structure at 0.03 <= x <= 0.05, and a single tetragonal phase structure at x=0.06. The morphotropic phase boundary (MPB) for the ceramics is identified in the composition range of 0.03 <= x <= 0.05. With increasing the LS content, both d(33) and k(p) of the ceramics firstly increase and then decrease. At x=0.05, d(33) and k(p) reach their maximum values which are 230 pC/N and 0.42, respectively. The To-t and T-c of the ceramics shift to the low temperature with the increasing of the LS content. The To-t and T-c of the ceramics are 455 and 215 degrees C at x=0, 385 and 150 degrees C at x=0.02, 370 and 75 degrees C at x=0.06, respectively.