Enhancement of piezoelectric properties and temperature stability by forming an MPB in KNN-based lead-free ceramics
Yue-Ming Li,Zong-Yang Shen,Fen Wu,Tie-Zheng Pan,Zhu-Mei Wang,Zu-Gui Xiao
DOI: https://doi.org/10.1007/s10854-013-1682-4
2013-12-19
Abstract:Abstract0.92(Na0.51K0.49−xLix)NbO3–0.02Bi0.5K0.5TiO3–0.06BaZrO3 (x = 0, 0.01, 0.02, 0.03, 0.04, and 0.05) lead-free piezoelectric ceramics were prepared by solid state reaction route. The effect of Li doping amount on the structure and electrical properties of the ceramics were investigated. All ceramics had pure perovskite structure, while the crystallographic symmetry changed from rhombohedral to tetragonal with the increase of Li doping amount. A PZT-like morphotropic phase boundary (MPB) with the coexistence of rhombohedral and tetragonal phases was identified in the composition of x = 0.03. As expected, the ceramics of the MPB composition showed optimal properties: piezoelectric coefficient d33 = 227 pC/N, planar electromechanical coupling coefficient kp = 39.3 %, dielectric permittivity ε33T/ε0$$ \varepsilon_{33}^{T} /\varepsilon_{0} $$ = 1,640, dielectric loss tanδ = 2.0 %, remnant polarization Pr = 13.3 μC/cm2, coercive field Ec = 1.53 kV/mm, and Curie temperature Tc = 253 °C. Together with good temperature stability to 200 °C, this KNN-based lead-free ceramics should be very promising for practical applications.
engineering, electrical & electronic,materials science, multidisciplinary,physics, condensed matter, applied