EFFECT OF HOLDING TIME DURING SINTERING ON DIELECTRIC AND PIEZOELECTRIC PROPERTIES OF 0.96KNN-0.04 LiSbO3 CERAMICS
R. WANG,Y. LI,Y. TIAN,Z. LI,,,,
DOI: https://doi.org/10.15251/djnb.2020.151.253
2020-01-01
Digest Journal of Nanomaterials and Biostructures
Abstract:K2CO3, Na2CO3, Li2CO3, Sb2O3 and Nb2O5 were used as the starting materials, the 0.96(Na0.5K0.5)NbO3-0.04LiSbO3 ceramics are prepared using solid state synthesis method, and effects of holding time during sintering on dielectric and piezoelectric properties of 0.96KNN-0.04 LiSbO3 ceramics are investigated. The crystal structure was detected using X-ray diffraction characterization, and the micrographs were observed by field emission scanning electron microscopy. The results show that the crystal structure for 0.96KNN-0.04 LiSbO3 ceramics with different holding time is all perovskite structure, with the extension of holding time, the proportion of the two diffraction peaks decreases gradually, and presents the trend of gradually merging into a single peak. With the extension of the holding time, the relative dielectric constant increases first and then decreases, reaching the maximum value of 1015 at 5 h. With the increase of holding time, the Curie temperature Tc moves to high temperature, Tc rises from 295 oC to 350 oC, at the same time, the dielectric constant at Curie point reaches 4869 when the holding time is 5 h. Afterwards, the piezoelectric constant increases first and then decreases with the increase of holding time, and the holding time is 5 h, d33 = 147 pC/N, reaching the maximum value. So the dielectric and piezoelectric properties of 0.96KNN-0.04 LiSbO3 ceramics are optimized when the holding time is 5 h.
materials science, multidisciplinary,nanoscience & nanotechnology