Fatigue fracture of 7B04 aluminum alloy under different stresses

Hai-gen JIAN,Feng JIANG,Kang WEN,Hong-feng HUANG,Li-li WEI,Long JIANG

2010-01-01

Abstract:The microstructures of fatigue fracture of Al alloys under various stresses were studied by optical microscope and scanning electron microscope, and the microscopic features of crack initiation and propagation in this kind of alloy were revealed. The results show that the fatigue cracks usually initiate at or near the free surfaces of the specimen. And with the increase of the loading stress, the distance between the crack and the surface decreases. The cracks are 250 μm in depth from the surface under strain of 285 MPa, while they are initiated at the free surface under 430 MPa. Striation can't be observed in the area near the crack source. Moreover, the area will be reduced with the increase of loading stress. In the crack propagation zone, there is a uniform increase in striation distance as the strain amplitude increases. After the formation of cracks, the micro cracks propagate towards the depth along the direction of maximum shear stress at an angle of 45° with the stress axis, and then they turn to the direction perpendicular to the stress axis and finally get fractured instantaneously. With the increase of stress, the area of propagation zone on the fracture surface reduces while the area of fatigue fracture zone is enlarged.