Comparative CH 4-sensing characteristic studies of PDMEB and PDMEB/in 2o 3 thin film sensors

Heng B. Hu,Guangzhong Xie,Ping Sun,Yadong Jiang,Huiling Tai

DOI: https://doi.org/10.1109/ICACIA.2010.5709860

2010-01-01

Abstract:In this paper, the poly-2, 5-dimethoxyethynylbenzene (PDMEB) and poly-2, 5-dimethoxyethynylbenzene/In 2O 3 were in-situ synthesized as gas sensing materials. The PDMEB/In 2O 3 nanocomposite was accessed by two procedures both relying on Pd catalysis: (1) The reaction of ethynyltri-n-buyltin replacing Br belonged to 1, 4-dibromo-2, 5-dimethoxy benzene, and (2) The step-growth polymerization of PDMEB through heating up the mixer, at the same time adding appropriate In 2O 3 nanoparticle. The morphology of films were characterized by scanning electron microscope(SEM). Compared with the pure PDMEB, it clearly appears that In 2O 3 components influence the morphology of the nanocomposite film, which leads to the variation of the response-recovery behavior of sensors. The PDMEB and PDMEB/In 2O 3 were deposited on the surface acoustic wave devices (SAW, whose corresponding operation frequency of baseline is 433.9MHz) to fabricate gas sensors by the spin-coating method. The sensors were exposed to various concentrations of CH 4 (in the range of 1%-5%) at room temperature, and the frequency shift of sensors were recorded. It was found that the PDMEB/In 2O 3 nanocomposite thin film sensor exhibited a better gas-sensing property than that of PDMEB thin film sensor. © 2010 IEEE.