Abstract:In this study, 9LiFePO4·Li3V2(PO4)3/C (LFVP-91/C) composite cathode materials (molar ratio of LiFePO4:Li3V2(PO4)3 = 9:1) were prepared using a sol–gel (SG) technique and spray drying (SP) technique, followed by a calcination process at 650–750 °C for 10 h. Oxalic acid and citric acid were used as chelating agents, l-ascorbic acid (AA) was used as a reducing agent, and sucrose (SUC) was used as a carbon source. For improving the electrochemical properties of LFVP-91/C, different conductive carbon materials were used as carbon additives, including graphene oxide (GO), graphene nanosheet (GNS), and carbon nanotube (CNT). The experimental results show that the best discharge capacities of as-prepared SG-LFVP-91/C are approximately 151.1 mAh/g at 0.1C/0.1C, 115.2 mAh/g at 0.2C/5C, and 98.2 mAh/g at 0.2C/10C. The capacity retention after 100 cycles at 1C/1C is 84.0%. After addition of GO, the best discharge capacity retention increases to 91.66% after 100 cycles at 1C/1C. Moreover, after addition of GNS + CNT, the discharge capacity of SP-LFVP-91/C/GNS + CNT composite material increases to 160.1 mAh/g at 0.1C/0.1C, 129.3 mAh/g at 0.2C/5C, and 117.8 mAh/g at 0.2C/10C. No capacity fading is observed after 30 cycles at 0.1C/0.1C. The capacity retentions after 100 cycles and 500 cycles at 1C/1C increase to 97.58% and 85.26%, respectively. This study demonstrates that the prepared SP-LFVP-91/C/GNS + CNT composite cathode materials are excellent candidates for use in lithium-ion power batteries for electric vehicles.

Improved Electrochemical Performances of 9lifepo4·li3v2(po4)/c Composite Prepared by a Simple Solid-State Method

High-performance Carbon-Coated LiMnPO4 Nanocomposites by Facile Two-Step Solid-State Synthesis for Lithium-Ion Battery

Improved Electrochemical Performances of LiFePO4·Li3V2(PO4)/C Composite Cathode Materials Prepared by Two Simple Solid-State Methods

Preparation of LiFePO4/Li3V2(PO4)3/C composite cathode materials and their electrochemical performance analysis

Material Optimization Engineering toward xLiFePO4·yLi3V2(PO4)3 Composites in Application-Oriented Li-Ion Batteries

Preparation of Li3V2 (po4)3/lifepo4 Composite Cathode Material for Lithium Ion Batteries

Electrochemical Performance of LiFe1−xVxPO4/carbon Composites Prepared by Solid-State Reaction

Optimized Performances of Core–shell Structured LiFePO4/C Nanocomposite

In Situ Low-Temperature Carbonization Capping of LiFePO4 with Coke for Enhanced Lithium Battery Performance

Facile fabrication of compact LiFePO4/C composite with excellent atomically-efficient for high-energy-density Li-ion batteries

LiFePO4/carbon Hybrids with Fast Li-ion Solid Transfer Capability Obtained by Adjusting the Superheat Temperature

Extra Li-ion storage of LiFePO4/C composite materials synthesized with Fe1.5P

Lifepo4/C Composite with 3d Carbon Conductive Network for Rechargeable Lithium Ion Batteries

Improvement of the Electrochemical Performance of LiFePO4 Cathode Composite Material Using a in Situ Pyrolysis Carbon Synthesis Procedure

Performance Enhancement of Lithium-Ion Battery with Lifepo4@C/Rgo Hybrid Electrode

LiFePO4/C composites with high compaction density as cathode materials for lithium-ion batteries with high volumetric energy density

Improving the Rate and Low-Temperature Performance of LiFePO 4 by Tailoring the Form of Carbon Coating from Amorphous to Graphene-Like

Synthesis and Electrochemical Performance of Xlifepo_4·yli_3v_2(po_4)_3 Composites

Improving the rate and low-temperature performance of LiFePO4 by tailoring the form of carbon coating from amorphous to graphene-like

Combined First-principles and Experimental Studies of a V- doped LiFePO4/C Composite as a Cathode Material for Lithium-ion Batteries

Enhanced electrochemical performance of LiVPO4F/C composite with in-situ generated Li3V2(PO4)3 for lithium-ion batteries