Abstract:A coordination-assisted synthetic approach is reported here for the synthesis of highly active and stable gold nanoparticle catalysts in ordered mesoporous carbon materials using triblock copolymer F127 as a structure-directing agent, thiol-containing silane as a coordination agent, HAuCl4 as a gold source, and phenolic resin as a carbon source. Upon carbonization, the gold precursor becomes reduced to form monodispersed Au nanoparticles of ca. 9.0 nm, which are entrapped or confined by the "rigid" mesoporous carbonaceous framework. Nanoparticle aggregation is inhibited even at a high temperature of 600 degrees C. After removal of the silica component, the materials possess the ordered mesostructure, high surface area (similar to 1800 m(2)/g), large pore volume (similar to 1.19 cm(3)/g), and uniform bimodal mesopore size (<2.0 and 4.0 nm). The monodispersed gold nanoparticles are highly exposed because of the interpenetrated bimodal pores in the carbon framework, which exhibit excellent catalytic performance. A completely selective conversion of benzyl alcohol in water to benzoic acid can be achieved at 90 degrees C and 1 MPa oxygen. Benzyl alcohol can also be quantitatively converted to benzoic acid at 60 degrees C even under an atmospheric pressure, showing great advantages in green chemistry. The catalysts are stable, poison resistant, and reusable with little activity loss due to metal leaching. The silane coupling agent played several functions in this approach: (1) coordinating with gold species by the thiol group to benefit formation of monodispersed Au nanopartides; (2) reacting with phenolic resins by silanol groups to form relatively "rigid" composite framework; (3) pore-forming agent to generate secondary pores in carbon pore walls, which lead to higher surface area, larger pore volumes, and higher accessibility to to the gold nanopartides. Complete removal of the silica component proves to have little effect on the catalytic performance of entrapped Au nanoparticles.

Porous gold nanobelts templated by metal-surfactant complex nanobelts.

Oxygenated Group and Structural Defect Enriched Carbon Nanotubes for Immobilizing Gold Nanoparticles

Electrochemical Fabrication of Nanoporous Gold

Controlled Synthesis of Gold Nanobelts and Nanocombs in Aqueous Mixed Surfactant Solutions

Nanoporous Gold Thin Film: Fabrication, Structure Evolution, and Electrocatalytic Activity

Synthesis of High Purity Au Nanobelts Via the One-Dimensional Self-Assembly of Triangular Au Nanoplates

Facile And Controllable Fabrication Of Gold Nanoparticles-Immobilized Hollow Silica Particles And Their High Catalytic Activity

Gold nanorod-templated synthesis of polymetallic hollow nanostructures with enhanced electrocatalytic performance.

Facile Preparation of Gold Nanoparticles Using the Self-Assembled ABC Non-Amphiphilic Fluorosilicone Triblock Copolymer Template

Fabrication of Oriented Arrays of Porous Gold Microsheaths Using Aligned Silver Nanowires As Sacrificial Template

Mesoporous silica-coating of gold nanorods by a templated method

Synthesis of Gold Nanoparticles by Using a Bolaform Schiff Base Amphiphile at Liquid-Liquid Interface

Synthesis of Gold Nanoshells Through Improved Seed-Mediated Growth Approach: Brust-like, in Situ Seed Formation

Gold Hierarchical Nanostructures Formed At The Solid/Liquid Interfaces Via Electroless Deposition And Their Sers Properties

Aggregation-Free Gold Nanoparticles In Ordered Mesoporous Carbons: Toward Highly Active And Stable Heterogeneous Catalysts

Bottom-Up then Top-Down Synthesis of Gold Nanostructures Using Mesoporous Silica-Coated Gold Nanorods

Gold Nanobipyramid-Embedded Silver-Platinum Hollow Nanostructures for Monitoring Stepwise Reduction and Oxidation Reactions.

Motif-mediated Au 25 (sph) 5 (pph 3 ) 10 X 2 Nanorods with Conjugated Electron Delocalization

Nanoporous gold with microporous structure prepared by sodium dodecyl sulfate-mediated electrochemical dealloying

The High Yield Synthesis and Characterization of Gold Nanoparticles with Superior Stability and Their Catalytic Activity

Ordered Array of Gold Nanoshells Interconnected with Gold Nanotubes Fabricated by Double Templating