Nanoporous gold with microporous structure prepared by sodium dodecyl sulfate-mediated electrochemical dealloying

Yaning Li,Guangzhong Li,Jian Wang

DOI: https://doi.org/10.1088/1361-6528/ad14b6

IF: 3.5

2023-12-13

Nanotechnology

Abstract:Nanoporous gold (NPG) is a promising catalytic material for the oxidation of CO and methanol applications. However, NPGs are prone to extensive macroscopic cracking that often decrease mechanic properties of NPG and depresses their catalytic effect. To produce crack-free NPG with an ultra-finer porosity in room temperature, the anionic surfactant sodium dodecyl sulfate (SDS) was added in electrochemical dealloying process. SDS has the effect of reducing the surface diffusion of gold which hinder the initial coarsening of ligaments and prevents interior silver atoms from being exposed and dissolved. As a result, the pore and ligment size are finer, but higher residual silver of NPG samples. NPG with pore size down to 2nm and the ligament 4.0 nm was successfully fabricated with 13.32 mM SDS in perchloric acid solution. The surface diffusion coefficient of Au atoms was 1.6 ×10−24 m2·s−1, nearly 3 orders of magnitude smaller than that of Au atoms in the absence of SDS (2.8 × 10−21 m2·s−1). Nanoindentation results demonstrate that high residual silver make NPG samples harder and stiffer,the specific surface areas of NPG with 6.66mM SDS is 190 m2g−1 by BET. This work provides very important clues on how to control the crack free ultrafine nanoporous structure of other materials.

materials science, multidisciplinary,physics, applied,nanoscience & nanotechnology