Abstract:Supported gold nanoparticles with sizes below 5 nm display attractive catalytic activities for heterogeneous reactions, particularly those promoted by secondary metal (e.g., Cu) because of the well-defined synergy between metal compositions. However, the specific atomic structure at interfaces is less interpreted systematically. In this work, various bimetallic Au-CuOx catalysts with specific surface structures were synthesized and explored by aberration-corrected scanning transmission electron microscopy (AC-STEM), temperature-programmed experiments and in situ DRIFT experiments. Results suggest that the atomic structure and interfaces between gold and CuOx are determined by the nucleation behaviors of the nanoparticles and result in subsequently the distinctive ability for CO activation. Bimetallic CuO*/Au sample formatted by gold particles surrounded with CuOx nanoclusters have rough surface with prominently exposed low-coordinated Au step defects. Whereas the bimetallic Au@CuO sample formatted by copper precursor in the presence of gold nanoparticles have core-shell structure with relatively smooth surface. The former structure of CuO*/Au displays much accelerated properties for CO adsorption and activation with 90% CO converted to CO2 at 90 °C and nice stability with time on stream. The results clearly determine from atomic scale the significance of exposed gold step sites and intrinsic formation of defected surface by different nucleation. The above properties are directly responsible for the induced variation in chemical composition and the catalytic activity.

Oxygenated Group and Structural Defect Enriched Carbon Nanotubes for Immobilizing Gold Nanoparticles

The role of surface chemistry of functionalized carbon nanotubes for immobilizing gold nanoparticles

Halloysite Nanotubes Supported Gold Catalyst for Cyclohexene Oxidation with Molecular Oxygen

Subnanometric Gold Clusters on CeO2 with Maximized Strong Metal–Support Interactions for Aerobic Oxidation of Carbon–Hydrogen Bonds

Gold/Platinum Hybrid Nanoparticles Supported on Multiwalled Carbon Nanotube/Silica Coaxial Nanocables: Preparation and Application As Electrocatalysts for Oxygen Reduction

Gold Cluster–CeO2 Nanostructured Hybrid Architectures As Catalysts for Selective Oxidation of Inert Hydrocarbons

Au Nanoparticles Anchored on Sulfonated Carbon Nanotubes for Benzyl Alcohol Oxidation

Modified Carbon Nanotubes: an Effective Way to Selective Attachment of Gold Nanoparticles

Low Temperature Co Oxidation Over Unsupported Nanoporous Gold

Rapid microwave-assisted synthesis and electrochemical characterization of gold/carbon nanotube composites

An Au22(L8)6 Nanocluster with in Situ Uncoordinated Au As a Highly Active Catalyst for O2 Activation and CO Oxidation

Carbon nanotubes decorated with Pt nanoparticles via electrostatic self-assembly: a highly active oxygen reduction electrocatalyst

Boosting the Catalytic Behavior and Stability of a Gold Catalyst with Structure Regulated by Ceria.

Oxygen Reduction Catalyzed by Gold Nanoclusters Supported on Carbon Nanosheets

Gold Nanoparticle/Multi-walled Carbon Nanotube Hybrid as a Stable Catalyst for the Oxygen Reduction Reaction

Porous Carbon-Supported Gold Nanoparticles for Oxygen Reduction Reaction: Effects of Nanoparticle Size.

Gold Nanocatalysts Supported on Protonic Titanate Nanotubes and Titania Nanocrystals

Carbon Nanotubes Decorated with Pt Nanocubes by a Noncovalent Functionalization Method and Their Role in Oxygen Reduction

Preparation and Electrocatalytic Activity of Gold Nanoparticles Immobilized on the Surface of 4-Mercaptobenzoyl-functionalized Multiwalled Carbon Nanotubes

Atomic-Scale Observation of Bimetallic Au-CuOx Nanoparticles and Their Interfaces for Activation of CO Molecules.

Highly Dispersed Gold Nanoparticles Anchoring on Post-Modified Covalent Organic Framework for Catalytic Application