Abstract:A novel hyperbranced azo polymer with terminal diazonium groups was synthesized by step-growth polymerization of 4,4'-diamino diphenyl sulphone's diazonium salts (A(2)) and benzene-1,3,5-triearboxylic acid tri2-(N-ethylanilino) ethyl ester (B-3) through azo-coupling reaction. 4, 4'-diamino diphenyl sulphone (0.248 g, I mmol) was dissolved in a hot homogeneous mixture of glacial acetic acid (7.5 mL) and sulfuric acid ( I mL). Aqueous solution of sodium nitrite (0.166 g, 2.4 mmol) in 0.5 mL water was added dropwise into the solution at 0 degrees C and kept at this temperature for 5 min. The diazonium salt solution of 4,4'-diamino diphenyl sulphone was then added dropwise into the solution of benzene-1, 3, 5-tricarboxylic acid tri-2-( N-ethylanilino) ethyl ester (0.326 g, 0.5 mmol) in 50 mL DMF at 0 degrees C. After the reaction was carried out at 0 degrees C for 8 h, the solution containing the diazonium-hyperbranched azo polymer was directly used as the polyeation solution. The purchased sodium polystrene sulfonate (PSSA) was used as polyanion. Then the multilayer films were prepared by an electrostatic layer-by-layer deposition method. The self-assembly processes and morphologies of surfaces were characterized by UV-Vis spectra, ellipsometer and AFM. A linear increase of absorbance and thickness was observed as the number of the bilayers increased. Dichroism was optically induced in the self-assembly film under the irradiation of a polarized Ar+ laser beam at 488 nm. After 15 min irradiation of the laser beam at an intensity of 80 mW/cm(2) the orientation order parameter of the multilayer film obtained was about 0.02. With interfering illumination of Ar+ laser beams for 30 min, significant surface relief gratings formed on the self-assembly multilayer film were observed. The spatial period and height of the obtained SRGs were about 744 nm and 20 nm. respectively.

Photolysis Kinetics of 4-(2-(4’-pyridinyl)ethynyl)benzenic Diazonium Salt and Characterization of Its Self-Assembled Monolayer Film

Full-conjugated Layer-by-layer Self-assembly Ultrathin Functional Films Fabricated from Terpyridine and Transition Metal Ions Based on Coordinate Interaction

Monitoring of the Photo Reaction of Self-Assembly Film Based on Diazoresin by FTIR

Self-Assembled Film of Poly(4-Carboxyphenyl)Acetylene and Diazoresin and Its Photoelectric Conversion Property

Fabrication and Optoelectronic Conversion of Layer-By-Layer Self-Assembly Films Based on Terpyridines and Metal Ions on Surface of Substrate Modified by Diazoresin and 4-Formylbenzoic Acid

Fabrication of a Covalently Attached Multilayer Via Photolysis of Layer-by-layer Self-Assembled Films Containing Diazo-Resins

Studies on the Molecular Environment and Reaction Kinetics of Photo-Oligomerization in Langmuir−Blodgett Films of 4-(4-(2-(octadecyloxycarbonyl)vinyl)- Cinnamoylamino)benzoic Acid

FABRICATION OF PHOTORESPONSIVE ELECTROSTATIC MULTILAYERS CONTAINING DIAZONIUM-HYPERBRANCHED AZO POLYMER

Fabrication of photosensitive self-assembled multilayer films based on porphyrin and diazoresin via H-bonding

Photo-Induced Dna Cleavage in Self-Assembly Multilayer Films

The Spectral And Electrochemical Properties Of Phenylazonaphthalene Based On Self-Assembled Monolayer

Investigation of the Covalently Attached Multilayer Architecture Based on Diazo-Resins and Poly(4-styrene sulfonate)

Self-Assembly Ultrathin Films Based on Diazoresins

Synthesis and non-linear optical properties of some organic self-assembled films on hydroxylated substrate surfaces

Design of Photochromic and Electrochemical Active Azosilane Self-Assembled Monolayer

Photoresponsive Layer-By-Layer Ultrathin Films Prepared from A Hyperbranched Azobenzene-Containing Polymeric Diazonium Salt

X-Ray Photoelectron Spectroscopy Study of the Deposition of Tio2 Thin Films on Self-Assembly Monolayer

Ultrathin Films Prepared from A Polystyrene-Based Polymeric Diazonium Salt Via Layer-By-Layer Self-Assembly

Synthesis And Characterization Of Conjugated Mono- And Dithiol Oligomers And Characterization Of Their Self-Assembled Monolayers

Diazonium-Functionalized Silicon Hybrid Photoelectrodes: Film Thickness and Composition Effects on Photoelectrochemical Behavior

Self-revealing Kinetically Captured Self-Assembly of a N,N′-diphenyl-dihydrodibenzo[a,c]phenazine Derivative