Ultrathin Films Prepared from A Polystyrene-Based Polymeric Diazonium Salt Via Layer-By-Layer Self-Assembly

Li Xinyang,Wang Xiaolin,Wang Yanmei,Tuo Xinlin,Wang Xiaogong

DOI: https://doi.org/10.3724/sp.j.1105.2010.09471

2010-01-01

Abstract:A polystyrene-based polymeric diazonium salt (PS-DAS) was used to demonstrate that its ultrathin films could be prepared through a sequential growth manner. The films were prepared by dipping the substrates in the PS-DAS solution,washing with deionized water, and drying repeatedly. The growing process of untrathin films was monitored by UV-Vis spectroscopy and ellipsometry. The surface morphology and wettability of the films were characterized by AFM and water contact angle measurements. Results showed that PS-DAS could form thin films through uniformly layer-by-layered growth manner by a repeated dipping-coating- drying process. The UV-Vis and ellipsometry results showed that the amount of PS-DAS adsorbed in each dipping cycle was almost the same. In the dipping-washing-drying cycles, the drying step after each deposition was critical for growth of the PS-DAS ultrathin film. After heating treatment, cross-linking occurred in the thin films. The water contact angle changed from 77 degrees to 90.7 degrees after heating, which indicated the decomposition of the diazonium functional groups. The solvent resistance of the PS-DAS ultrathin films was also greatly enhanced by cross-linking. The observations are helpful for understanding the unique self-assembling properties of polymeric diazonium salt which could be used to prepare ultrathin films.