Abstract:SAPO-34 catalysts, used in methanol to olefins (MTO), with different n (SiO 2) : n(Al 2O 3) (0.15-0.80) were prepared hydrothermally with tetraethyl ammonium hydroxide and triethylamine as templates. The SAPO-34 catalysts were characterized by means of XRD, SEM, BET and NH 3-TPD. The results indicated that when n(SiO 2) : n(Al 2O 3) was 0.30, crystallinity of the prepared catalyst was maximal, and its specific surface area and crystallite size range were 490 m 2/g and 0.6-1.5 μm respectively. With increase of n(SiO 2) : n(Al 2O 3), crystallinity and crystallite size of the catAlysts decreased, but its specific surface area increased. Under optimal MTO conditions: temperature 425°C, methanol WHSV 1 h -1 and n(SiO 2) : n(Al 2O 3) of SAPO-34 catalyst, conversion of methanol, the total selectivity to ethylene and propylene, and lifetime of the catalyst could reached 100.0%, 86.87% and 546 min, respectively. With increase of n (SiO 2) : n (Al 2O 3), the tot Al selectivity to ethylene and propylene and the lifetime of the catalysts All reduced.

Performances of SAPO-34 Catalysts with Different Ratios of Si to Al in Methanol-to-Olefins