Abstract:Novel and uniform mesoporous silica particles with controllable cavities in their surface have been fabricated using PAA and CTAB as dual templates in a mild reaction system. Herein, a series of hierarchically distinct silica particles can be obtained by simply adjusting the mass ratios (R) of PAA to CTAB. When the R value continues to decrease, the corresponding number and opening size of these cavities are also increased. However, if no PAA added, only unique monodisperse mesoporous silica spheres with uniform size of approximately 400 nm can be obtained. These specific silica particles were characterized by means of small-angle X-ray diffraction (XRD), scanning electron microscope (SEM), transmission electron microscope (TEM), Fourier-transform infrared (FT-IR) spectra, and nitrogen adsorption-desorption measurements. Results show that these unique mesoporous silica particles totally behave as an hexagonally ordered mesophase. The maximum BET surface area can be as high as 891 m(2)/g, and the maximum pore volumes can be as large as 0.27 cm(3)/g. Notably, the specific cavity features including opening size and cavity number almost do not change after calcination treatment. Moreover, a possible formation mechanism of the hierarchically distinct silica particles has been put forward, considering that the specific interface instability effect, the reduction in the surface free energy, and the synergic self-assembly of PAA and CTAB in solution can play a key role in mediating the formation of the hierarchical silica nanostructures. In general, the synthesis route is simple and straightforward for the preparation of the other biomineral nanostructures and may play an important role in microencapsulation.

Hollow Carved Single-Crystal Mesoporous Silica Templated by Mesomorphous Polyelectrolyte−Surfactant Complexes

"Noodle-Like" Mesoporous Silica Templated By Polyelectrolyte/Surfactant Complex

Hierarchical porous structures by using zeolite nanocrystals as building blocks

Double-Templating Synthesis of Hierarchical Meso-Macroporous Silica Monolith

Highly efficient synthesis of ordered mesoporous silica materials with controllable microporosity using surfactant mixtures as templates

Template Synthesis of 3-D Bimodal Ordered Porous Silica

A Systematic Investigation Of The Formation Of Ordered Mesoporous Silicas Using Poly(Ethylene Oxide)-B-Poly(Methyl Methacrylate) As The Template

Tunable Hierarchical Porous Silica Materials Using Hydrothermal Sedimentation-Aggregation Technique

Nonionic Block Copolymer and Anionic Mixed Surfactants Directed Synthesis of Highly Ordered Mesoporous Silica with Bicontinuous Cubic Structure

Ordered mesoporous polymers and polymer-silica anocomposites

Hierarchically Porous Silica with Ordered Mesostructure from Confinement Self-Assembly in Skeleton Scaffolds

Mesoporous MFI zeolites with self-stacked morphology templated by cationic polymer.

Mesoporous silicas of hierarchical structure by hydrothermal surfactant-templating under mild alkali conditions

Single-strand Spider Silk Templating for the Formation of Hierarchically Ordered Hollow Mesoporous Silica Fibers

Synthesis of Hollow Mesoporous Silica Spheres with Radially Aligned Mesochannels and Tunable Textural Properties

Triblock Copolymer and Poly(Ethylene Glycol) As Templates for Monolithic Silica Material with Bimodal Pore Structure

Facile synthesis of hierarchically mesoporous silica particles with controllable cavity in their surfaces.

Facile Synthesis of Hierarchically Porous Carbons from Dual Colloidal Crystal/Block Copolymer Template Approach

Syntheses of High-Quality Mesoporous Materials Directed by Blends of Nonionic Amphiphiles under Nonaqueous Conditions

One-Pot Preparation of Hollow Silica Spheres by Using Thermosensitive Poly(N-Isopropylacrylamide) As A Reversible Template

Spontaneous Preparation Of Hierarchically Porous Silica Monoliths With Uniform Spherical Mesopores Confined In A Well-Defined Macroporous Framework